| About |
|---|
| High impact ABS for sheet extrusion and blow molding applications.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | ABS |
| Material Status | Commercial: Active |
| Features | High impact resistance,HB |
| Availabilitys | North America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| IMPACT | Nominal value | Unit | Test method |
| Charpy Notched Impact Strength | |||
| 23℃ | 37 | kJ/m² | ISO 179/1eA |
| Impact strength of cantilever beam notch | ASTM D256 | ||
| -30℃ | 300 | J/m | ASTM D256 |
| 23℃ | 430 | J/m | ASTM D256 |
| Impact strength of cantilever beam notch | ISO 180/1A | ||
| -30℃ | 23 | kJ/m² | ISO 180-1A |
| 23℃ | 35 | kJ/m² | ISO 180-1A |
| Dart impact equipped with measuring instruments | |||
| 23℃，Total Energy | 37.0 | J | ASTM D3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 64 mm span | 78.0 | ℃ | ISO 75-2/Af |
| 1.8 MPa, unannealed, 3.2 mm | 76.0 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed, 3.2 mm | 91.0 | ℃ | ASTM D648 |
| Vicat Softening Temp | 106 | ℃ | ASTM D1525 10 |
| Vicat Softening Temp | |||
| B50 | 95.0 | ℃ | ISO 306 |
| B120 | 97.0 | ℃ | ISO 306/B120 |
| Linear coefficient of thermal expansion | |||
| TD：-40~40℃ | 1.0E-4 | 1/℃ | ASTM E831 |
| MD：-40~40℃ | 1.0E-4 | 1/℃ | ASTM E831 |
| Relative temperature index | |||
| Electrical performance | 60.0 | ℃ | UL 746 |
| Strength mechanical performance | 60.0 | ℃ | UL 746 |
| Impact mechanical performance | 60.0 | ℃ | UL 746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Arc resistance | PLC 5 | ASTM D495 | |
| Compared to the leakage tracing index | PLC 0 | UL 746 | |
| High Arc Burning Index (HAI) | PLC 4 | UL 746 | |
| High voltage arc marking rate | |||
| HVTR | PLC 1 | UL 746 | |
| Hot wire ignition | |||
| HWI | PLC 4 | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.50 mm | HB | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 2080 | MPa | ASTM D638 |
| Tensile modulus | 1970 | MPa | ISO 527-1-2 |
| tensile strength | |||
| fracture | 30.0 | MPa | ASTM D638 |
| fracture | 30.0 | MPa | ISO 527-2/50 |
| yield | 41.0 | MPa | ISO 527-2/50 |
| yield | 39.0 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 21 | % | ISO 527-2/50 |
| fracture | 32 | % | ASTM D638 |
| yield | 2.6 | % | ISO 527-2/50 |
| yield | 3.1 | % | ASTM D638 |
| Bending modulus | 2000 | MPa | ISO 178 |
| 50 mm span | 2160 | MPa | ASTM D790 |
| bending strength | 60.0 | MPa | ISO 178 |
| bending strength | |||
| Yield, 50 mm span | 66.0 | MPa | ASTM D790 |
| Rockwell hardness | |||
| R-level | 102 | ASTM D785 |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Density | 1.03 | g/cm³ | ASTM D792 |
| Density | 1.03 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 220℃，10.0kg | 4.0 | g/10min | ISO 1133 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.60 to 0.80 | % | Internal Method |
| Apparent viscosity of melt | |||
| 240℃，100 sec^-1 | 1550 | Pa·s | ASTM D3835 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Drying temperature | 82 to 93 | °C | |
| Drying time | 4.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Barrel 1 zone temperature | 171 to 199 | °C | |
| Barrel 2 zone temperature | 182 to 221 | °C | |
| Barrel 3 zone temperature | 188 to 227 | °C | |
| Barrel 4 zone temperature | 199 to 238 | °C | |
| Connector temperature | 204 to 249 | °C | |
| Melt temperature | 216 to 260 | °C | |
| Nozzle temperature | 204 to 249 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.20 in/min |
| 3. Type I, 0.20 in/min |
| 4. 0.051 in/min |
| 5. 0.079 in/min |
| 6. Yield |
| 7. 80*10*4 sp=62mm |
| 8. 80*10*4 |
| 9. 80*10*4 mm |
| 10. Rate B (120°C/h), Loading 2 (50 N) |
| 11. Tungsten Electrode |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |