| About |
|---|
| Flame retardant ABS. Excellent indoor UV properties. Excellent moldability. UL94V-0/5VA rated. Elevated UL RTI rating.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Material Status | Commercial: Active |
| Features | 5VA,Flame Characteristics,Excellent Processability,V-0,Weather resistance is good |
| Availabilitys | North America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| MECHANICAL | Nominal value | Unit | Test method |
| Tensile modulus | 2070 | MPa | ASTM D638 |
| Tensile modulus | 2210 | MPa | ISO 527-1-2 |
| tensile strength | |||
| fracture | 30.3 | MPa | ASTM D638 |
| yield | 37.9 | MPa | ASTM D638 |
| yield | 41.1 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| fracture | 17 | % | ASTM D638 |
| fracture | 22 | % | ISO 527-2/50 |
| yield | 2.4 | % | ASTM D638 |
| Bending modulus | 2260 | MPa | ISO 178 |
| 50 mm span | 2340 | MPa | ASTM D790 |
| bending strength | 63.3 | MPa | ISO 178 |
| bending strength | |||
| Yield, 50 mm span | 67.6 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 12 | kJ/m² | ISO 180-1A |
| 23℃ | 210 | J/m | ASTM D256 |
| Dart impact equipped with measuring instruments | |||
| 23℃，Total Energy | 28.5 | J | ASTM D3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 3.2 mm | 75.0 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed, 3.2 mm | 86.1 | ℃ | ASTM D648 |
| Vicat Softening Temp | 93.9 | ℃ | ASTM D1525 8 |
| B50 | 92.0 | ℃ | ISO 306 |
| Linear coefficient of thermal expansion | |||
| TD：-40~40℃ | 9.2E-5 | 1/℃ | ASTM E831 |
| MD：-40~40℃ | 9.0E-5 | 1/℃ | ASTM E831 |
| Relative temperature index | |||
| Electrical performance | 90.0 | ℃ | UL 746 |
| Strength mechanical performance | 90.0 | ℃ | UL 746 |
| Impact mechanical performance | 85.0 | ℃ | UL 746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | > 1.0E+14 | ohms·cm | IEC 60093 |
| Dielectric strength | |||
| 3.2 mm in oil | 20 | kV/mm | IEC 60243-1 |
| Arc resistance | PLC 7 | ASTM D495 | |
| Compared to the leakage tracing index | PLC 1 | UL 746 | |
| High Arc Burning Index (HAI) | PLC 4 | UL 746 | |
| High voltage arc marking rate | |||
| HVTR | PLC 4 | UL 746 | |
| Hot wire ignition | |||
| HWI | PLC 2 | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 1.50 mm | V-0 | UL 94 | |
| 2.80 mm | 5VA | UL 94 |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Density | 1.19 | g/cm³ | ASTM D792 |
| Density | 1.19 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 230℃，3.80kg | 3.3 | g/10min | ASTM D1238 |
| 220℃，5.0kg | 7.0 | g/10min | ISO 1133 |
| Melt Volume Rate | |||
| 220℃，10 kg | 40.0 | cm³/10min | ISO 1133 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.50 to 0.70 | % | Internal Method |
| Apparent viscosity of melt | |||
| 200℃，1000 sec^-1 | 320 | Pa·s | ASTM D3835 |
| Process Conditions | |||
|---|---|---|---|
| Injection | Nominal value | Unit | Test method |
| drying temperature | 82 to 88 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Drying time, maximum | 8.0 | hr | |
| Recommended maximum moisture content | 0.10 | % | |
| Suggested injection volume | 50 to 70 | % | |
| Temperature at the rear of the barrel | 171 to 182 | °C | |
| Temperature in the middle of the barrel | 199 to 210 | °C | |
| Front temperature of material barrel | 204 to 221 | °C | |
| Nozzle temperature | 204 to 232 | °C | |
| Processing (melt) temperature | 204 to 232 | °C | |
| Mold temperature | 49 to 71 | °C | |
| Back pressure | 0.345 to 0.689 | MPa | |
| Screw speed | 30 to 60 | rpm | |
| Exhaust hole depth | 0.038 to 0.051 | mm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.20 in/min |
| 3. Type I, 0.20 in/min |
| 4. 0.051 in/min |
| 5. 0.079 in/min |
| 6. Yield |
| 7. 80*10*4 |
| 8. Rate B (120°C/h), Loading 2 (50 N) |
| 9. Tungsten Electrode |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |