CYCOLAC™ G365 resin

About

Product Description
Supplier	SABIC
Generic	ABS
Material Status	Commercial: Active
Availabilitys	North America,Latin America

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.05		ISO 1183
Shrinkage rate
MD	0.5~0.7	%
Melt Flow Rate
220℃，10.0kg	6	g/10min	ISO 1133
Melt Volume Rate
220℃，10 kg	6	cm³/10min	ISO 1133
Water absorption rate
Saturation, 23 ℃	1	%	ISO 62
23℃，50% RH	0.2	%	ISO 62

MECHANICAL	Nominal value	Unit	Test method
Taber wear (CS-17, 1 kg)	100	mg/1000cy
tensile strength
Yield, 5 mm/min	45	MPa	ISO 527
Fracture, 5 mm/min	35	MPa	ISO 527
Yield, 50 mm/min	50	MPa	ISO 527
Fracture, 50 mm/min	40	MPa	ISO 527
Tensile strain
Yield, 5 mm/min	3	%	ISO 527
Fracture, 5 mm/min	10	%	ISO 527
Yield, 50 mm/min	3	%	ISO 527
Fracture, 50 mm/min	10	%	ISO 527
Tensile modulus	2500	MPa	ISO 527
bending strength
yield	75	MPa	ISO 178
Bending modulus	2500	MPa	ISO 178
Rockwell hardness
R-level	115		ISO 2039-2
Hardness, H358/30	93	MPa	ISO 2039-1

THERMAL	Nominal value	Unit	Test method
Vicat Softening Temp
B50	108	℃	ISO 306
B120	110	℃	ISO 306
Hot deformation temperature
0.45 MPa	102	℃	ASTM D648
1.8 MPa	85	℃	ASTM D648
Thermal conductivity coefficient	0.2	W/m/℃	ISO 8302
Linear expansion coefficient (23 ℃~60 ℃)
MD	8×10^-5	1/°C	ISO 11359-2
TD	8×10^-5	1/°C	ISO 11359-2
Ball pressure test
75℃±2℃	PASSES		IEC 60695-10-2
Maximum approximation value	100	℃	IEC 60695-10-2
Relative temperature index
Electrical performance	80	℃	UL 746B
Impact mechanical performance	80	℃	UL 746B
Non mechanical impact performance	80	℃	UL 746B

IMPACT	Nominal value	Unit	Test method
Impact strength of cantilever beam notch
23℃	11	kJ/m²	ISO 180-1A
-30℃	6	kJ/m²	ISO 180-1A
Charpy Notched Impact Strength
23℃	11	kJ/m²	ISO 179/1eA
-30℃	6	kJ/m²	ISO 179/1eA

Electrical performance	Nominal value	Unit	Test method
Volume resistivity	>1×10^15	ohms·cm	IEC 60093
Surface resistivity	1E+15	ohms	IEC 60093
Dielectric strength
0.8 mm in oil	35	kV/mm	IEC 60243-1
1.6 mm in oil	26	kV/mm	IEC 60243-1
3.2 mm in oil	18	kV/mm	IEC 60243-1
Relative permittivity
50-60 Hz	2.8		IEC 60250
1 MHz	2.7		IEC 60250
Dissipation factor
50-60 Hz	0.011		IEC 60250
1 MHz	0.015		IEC 60250
Compared to the leakage tracing index	575	V	IEC 60112

FLAME CHARACTERISTICS	Nominal value	Unit	Test method
Flame retardant level
1.50 mm	HB		UL 94
3.00 mm	HB		UL 94

Pass at 650 ° C	3.2	mm	IEC 60695-2-12
750 ° C Passing	1	mm	IEC 60695-2-12
FMVSS combustion speed, thickness 1mm	25	mm/min	FMVSS 302

Process Conditions
injection molding	Nominal value	Unit	Test method
Dry conditions	Nominal value	Unit	Test method
Melt Temperature	250~280	℃
Nozzle temperature	245~275	℃
Front temperature	250~280	℃
Mid section temperature	250~280	℃
Post stage temperature	230~260	℃
Hopper temperature	60~80
Mold temperature	40~80	℃
drying temperature	90~100	℃
Drying time	2~4	hrs
Maximum moisture content	0.1	%

Notes
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.