| CYCOLAC™ INP564 resin High flow, low molecular weight powder SAN for color concentrates & alloys.&&CYCOLAC™ INP564 resin SABIC INP564 provides compatibility with a wider range of ABS grades than many color concentrate bases; allows better dispersion than pellets; allows concentrate manufacturers to produce both pelletized and dry blend concentrate; provides a base resin with less heat history than pellets; suitable for direct weather exposure; can be used in all SAN applications where a fine particle size is desired&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | SAN |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,High liquidity,Low molecular weight |
| Availabilitys | North America,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.08 | g/cm³ | ASTM D792 |
| Density | 1.07 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 230℃，3.80kg | 38 | g/10min | ASTM D1238 |
| 220℃，10.0kg | 78 | g/10min | ISO 1133 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 1.1 | kJ/m² | ISO 179/2C |
| Impact strength of cantilever beam notch | ASTM D256 | ||
| -30℃ | 22 | J/m | ASTM D256 |
| 23℃ | 14 | J/m | ASTM D256 |
| Impact strength of cantilever beam notch | ISO 180/1A | ||
| -30℃ | 2.5 | kJ/m² | ISO 180-1A |
| 23℃ | 1.9 | kJ/m² | ISO 180-1A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 64 mm span | 85.3 | ℃ | ISO 75-2/Af |
| 1.8 MPa, unannealed, 3.2 mm | 83.4 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed, 3.2 mm | 95.2 | ℃ | ASTM D648 |
| Vicat Softening Temp | |||
| B50 | 102 | ℃ | ISO 306 |
| B120 | 104 | ℃ | ISO 306/B120 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 3890 | MPa | ASTM D638 |
| Tensile modulus | 3840 | MPa | ISO 527-1-2 |
| tensile strength | |||
| fracture | 54.1 | MPa | ISO 527-2/50 |
| fracture | 53.6 | MPa | ASTM D638 |
| yield | 52.0 | MPa | ASTM D638 |
| yield | 54.1 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| fracture | 1.7 | % | ASTM D638 |
| fracture | 1.2 | % | ISO 527-2/50 |
| yield | 1.2 | % | ISO 527-2/50 |
| yield | 1.6 | % | ASTM D638 |
| Bending modulus | 3460 | MPa | ISO 178 |
| 50 mm span | 3720 | MPa | ASTM D790 |
| bending strength | 65.4 | MPa | ISO 178 |
| bending strength | |||
| Yield, 50 mm span | 82.5 | MPa | ASTM D790 |
| Rockwell hardness | |||
| R-level | 123 | ASTM D785 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |