| About |
|---|
| Low molecular weight SAN pellets.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | SAN |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,High molecular weight,Good melt strength,Low molecular weight |
| Availabilitys | North America,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.08 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Flow Rate | |||
| 230℃，3.80kg | 5.9 | g/10min | ASTM D1238 |
| 220℃，10.0kg | 16 | g/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Bending modulus | |||
| 50 mm span | 3900 | MPa | ASTM D790 |
| — | 3460 | MPa | ISO 178 |
| bending strength | |||
| — | 92.0 | MPa | ISO 178 |
| Yield, 50 mm span | 134 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Unnotch Impact strength | |||
| 23℃ | 1.4 | kJ/m² | ISO 179/2U |
| Impact strength of cantilever beam notch | |||
| 23℃ | 46 | J/m | ASTM D256 |
| -30℃ | 2.0 | kJ/m² | ISO 180-1A |
| 23℃ | 3.2 | kJ/m² | ISO 180-1A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed, 3.2 mm | 95.9 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 3.2 mm | 85.4 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 64 mm span | 88.0 | ℃ | ISO 75-2/Af |
| Vicat Softening Temp | |||
| B50 | 103 | ℃ | ISO 306 |
| B120 | 105 | ℃ | ISO 306/B120 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.051 in/min |
| 3. 0.079 in/min |
| 4. Yield |
| 5. 80*10*4 |
| 6. 80*10*4 mm |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |