| About |
|---|
| Product Description | |
|---|---|
| Supplier | SABIC |
| Material Status | Commercial: Active |
| Features | High impact resistance,Good liquidity |
| Availabilitys | Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.04 | g/cm³ | ISO 1183 |
| Melt Volume Rate | |||
| 220℃，10 kg | 39.0 | cm³/10min | ISO 1133 |
| Shrinkage rate | |||
| TD | 0.50 to 0.70 | % | Internal Method |
| Water Absorption | |||
| Equilibrium, 23 ℃, 50% RH | 0.16 | % | ISO 62 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -30℃ | 10 | kJ/m² | |
| 23℃ | 23 | kJ/m² | |
| Izod Notched Impact strength | |||
| -30℃ | 7.0 | kJ/m² | |
| 23℃ | 18 | kJ/m² |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature HDT | |||
| 0.45 MPa, unannealed, 100 mm span | 91.0 | ℃ | ISO 75-2/Be |
| 1.8 MPa, unannealed, 100 mm span | 80.0 | ℃ | ISO 75-2/Ae |
| Vicat Softening Temperature | |||
| — | 99.0 | ℃ | ISO 306 |
| — | 100 | ℃ | ISO 306/B120 |
| Coeff. of linear thermal expansion | |||
| Flow: 23~60 ℃ | 8.7E-5 | 1/℃ | |
| TD：23~60℃ | 8.7E-5 | 1/℃ |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Glow Wire Flammability Index GWFI | |||
| 3.2 mm | 650 | ℃ | IEC 60695-2-12 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 129 | ISO 2039-2 | |
| Ball indentation hardness | 95.0 | MPa | ISO 2039-1 |
| Tensile Modulus | 2400 | MPa | ISO 527-1-2 |
| Tensile Stress | |||
| yield | 40.0 | MPa | ISO 527-2/5 |
| yield | 45.0 | MPa | ISO 527-2/50 |
| fracture | 35.0 | MPa | ISO 527-2/5 |
| Tensile Strain | |||
| yield | 2.0 | % | ISO 527-2/5 |
| yield | 2.2 | % | ISO 527-2/50 |
| fracture | 35 | % | ISO 527-2/5 |
| fracture | 45 | % | ISO 527-2/50 |
| Flexural Modulus | 2450 | MPa | ISO 178 |
| Flexural Stress | 65.0 | MPa | ISO 178 |
| Process Conditions | |||
|---|---|---|---|
| Injection Molding | Nominal value | Unit | Test method |
| Drying Temperature | 85 to 95 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Maximum Moisture Content | 0.10 | % | |
| Hopper Temperature | 60 to 80 | °C | |
| Rear Temperature Zone 1 | 200 to 240 | °C | |
| Middle Temperature Zone 2 | 220 to 260 | °C | |
| Front Temperature Zone 3 | 220 to 260 | °C | |
| Nozzle temperature | 210 to 250 | °C | |
| Melt Temperature | 220 to 260 | °C | |
| Mold Temperature | 40 to 80 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |