Cycololoy™ CH6410 resin

About
CH6410是一种高温、冲击改性的PC树脂，具有非溴化、非氯化阻燃系统,只有有限的颜色

Product Description
Supplier	SABIC
Generic	PC+ABS
Material Status	Commercial: Active
Features	High impact resistance,Halogen free
Availabilitys	North America

Technical Data
MECHANICAL	Nominal value	Unit	Test method
tensile strength
Yield, 50 mm/min	63	MPa	ISO 527
Fracture, 50 mm/min	55	MPa	ISO 527
Tensile strain
Yield, 50 mm/min	5	%	ISO 527
Fracture, 50 mm/min	95	%	ISO 527
Tensile modulus
1 mm/min	2300	MPa	ISO 527
bending strength
Yield, 2 mm/min	90	MPa	ISO 178
Bending modulus
2 mm/mim	2400	MPa	ISO 178
Ball hardness
H358/30	100	MPa	ISO 2039-1

IMPACT	Nominal value	Unit	Test method
Total energy of instrument impact
23℃	74	J	ASTM D 3763
Impact strength of cantilever beam notch
23℃	920	J/m	ASTM D4812
23℃，80104	50	kJ/m²	ISO 180-1A
0℃，80104	19
80104 -30℃	15	kJ/m²	ISO 180-1A
Charpy Notched Impact Strength
80 * 10 * 3, 62mm span
23℃	55	kJ/m²	ISO 179/1eA
-30℃	15	kJ/m²	ISO 179/1eA

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
0.45 MPa, 100 mm span	126	℃	ISO 75/Be
1.8 MPa, 100 mm span	113	℃	ISO 75/Ae
Unannealed, 6.4 mm
0.45 MPa	127	℃	ASTM D 648
1.8MPa	118	℃	ASTM D 648
Linear expansion coefficient, -40 ℃ to 40 ℃
flow	7.74E-05	1/℃	ASTM E 831
transverse	5.94E-05	1/℃	ASTM E 831
Linear expansion coefficient, 23 ℃ to 60 ℃
flow	7.E-05	1/℃	ISO 11359-2
transverse	7.E-05	1/℃	ISO 11359-2
Vicat Softening Temp
B50	134	℃	ISO 306
B120	135	℃	ISO 306
Ball pressure test
125℃±2℃	PASSES		IEC 60695-10-2

PHYSICAL	Nominal value	Unit	Test method
Density	1.19		ASTM D792
Shrinkage rate
MD	0.05 – 0.07	%	Internal Method
Shrinkage rate
MD：3.2 mm	0.4 – 0.5	%	Internal Method
Melt Flow Rate
260℃，2.16kg	6.3	g/10min	ASTM D1238
Density	1.2		ISO 1183
Melt Volume Rate
300℃，2.16 kg	16	cm³/10min	ISO 1133

Electrical performance	Nominal value	Unit	Test method
Dielectric strength
3.2 mm in oil	18	kV/mm	IEC 60243-1
Relative permittivity
50-60 Hz	2.7		IEC 60250
1 MHz	2.7		IEC 60250
Dissipation factor
50-60 Hz	0.001		IEC 60250
1 MHz	0.1		IEC 60250
Volume resistivity	>1.E+15	ohms·cm	IEC 60093
Surface resistivity
ROA	>1.E+15	ohms	IEC 60093
Compared to the leakage tracing index	225		IEC 60112

FLAME CHARACTERISTICS	Nominal value	Unit	Test method
94v-1 flame level assessment	0.99	mm	UL 94
94V-0 flame level assessment	1.49	mm	UL 94

Process Conditions
injection molding	Nominal value	Unit	Test method
Drying temperature	90 – 100
Drying time	2 – 4	hrs
Drying time (cumulative)	8	hrs
Maximum water content	0.04	%
Melt temperature	270 – 300	°C
Nozzle temperature	265 – 300	°C
Front Section Zone 3 Temperature	265 – 300	°C
Temperature in Zone 2 of the middle section	260 – 300	°C
Temperature in Zone 1 of the rear section	260 – 300	°C
Mold temperature	60 – 90	°C
Back pressure	0.3 – 0.7	MPa
Screw speed	40 – 70	rpm
Shoot to cylinder size	40 – 80	%
Depth of exhaust groove	0.025 – 0.076	mm

Notes
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.