CYCOLOY™ C1100 resin

About
在低温下优良的延展性和耐热性

Product Description
Supplier	SABIC
Generic	PC+ABS
Material Status	Commercial: Active
Features	Heat Resistance, Good,Low temperature ductility
Availabilitys	Africa & Middle East ,Asia Pacific,Europe

Technical Data
MECHANICAL	Nominal value	Unit	Test method
Rockwell hardness
R-level	117		ISO 2039-2
Taber wear and tear
CS-17，1kg	79	mg/1000cy	Internal Method
tensile strength
Yield, 50 mm/min	55	MPa	ISO 527
Fracture, 50 mm/min	45	MPa	ISO 527
Tensile strain
Yield, 50 mm/min	4	%	ISO 527
Fracture, 50 mm/min	>50	%	ISO 527
Tensile modulus
1 mm/min	2400	MPa	ISO 527
bending strength
Yield, 2 mm/min	75	MPa	ISO 178
Bending modulus
2 mm/mim	900	MPa	ISO 178
tensile strength
Yield, 5 mm/min	45	MPa	ISO 527
Fracture, 5 mm/min	40	MPa	ISO 527
Tensile strain
Yield, 5 mm/min	4	%	ISO 527
Fracture, 5 mm/min	80	%	ISO 527
Ball hardness
H358/30	96	MPa	ISO 2039-1

IMPACT	Nominal value	Unit	Test method
Impact strength of cantilever beam notch
23℃，80103	450	J/m	ISO 180-1A
-30℃，80103	150	J/m	ISO 180-1A
Notched impact strength of cantilever beam
23℃，80104	NB	kJ/m²	ISO 180/1U
-30℃，80104	NB	kJ/m²	ISO 180/1U
Impact strength of cantilever beam notch
23℃，80104	41	kJ/m²	ISO 180-1A
80104 -30℃	17	kJ/m²	ISO 180-1A
Charpy Notched Impact Strength
23℃，80103	45	kJ/m²	ISO 179/1eA
-30℃，80103	15	kJ/m²	ISO 179/1eA
Charpy Notched Impact Strength
23℃，80104	42	kJ/m²	ISO 179/1eA
-30℃，80104	20	kJ/m²	ISO 179/1eA

THERMAL	Nominal value	Unit	Test method
Thermal conductivity coefficient	0.2	W/m/℃	ISO 8302
Linear expansion coefficient, from 23 ℃ to 60 ℃
flow	8.E-05	1/℃	ISO 11359-2
transverse	8.E-05	1/℃	ISO 11359-2
Ball pressure test
Maximum approximation value	110		IEC 60695-10-2
Vicat Softening Temp
B50	120	℃	ISO 306
B120	123	℃	ISO 306
Relative temperature index
Electrical performance	60	℃	UL 746B
Impact mechanical performance	60	℃	UL 746B
Non mechanical impact performance	60	℃	UL 746B
Hot deformation temperature
0.45 MPa, 100 mm span	120	℃	ISO 75/Be
1.8 MPa, 100 mm span	100	℃	ISO 75/Ae

PHYSICAL	Nominal value	Unit	Test method
Shrinkage rate
MD：3.2 mm	0.5 – 0.7	%	Internal Method
Density	0.04	g/cm³	ISO 1183
Water absorption rate
Equilibrium, 23 ℃	0.6	%	ISO 62
23℃，50% RH	0.2	%	ISO 62
Melt Volume Rate
260℃，5 kg	14	cm³/10min	ISO 1133

Electrical performance	Nominal value	Unit	Test method
Dielectric strength
In oil			ASTM D149
Relative permittivity
0.8 mm	35	kV/mm	IEC 60243-1
50-60 Hz	2.8		IEC 60250
1.6mm	25	kV/mm	IEC 60243-1
1 MHz	2.7		IEC 60250
Dissipation factor
3.2mm	17	kV/mm	IEC 60243-1
50-60 Hz	0.002		IEC 60250
1 MHz	0.007		IEC 60250
Volume resistivity	> 1.E+15	ohms·cm	IEC 60093
Surface resistivity	>1.0E+15		IEC 60093
Compared to the leakage tracing index
CTI	250	V	IEC 60112

FLAME CHARACTERISTICS	Nominal value	Unit	Test method
94HB flame rating assessment	0.059	mm	UL 94
94HB flame rating evaluation second reference value	0.118	mm	UL 94
Glowing wire flammability index
650 ℃, passed through	0.039	mm	IEC 60695-2-12

Process Conditions
injection molding	Nominal value	Unit	Test method
Drying temperature	95 – 105	°C
Drying time	2 – 4	hrs
Maximum water content	0.02	%
Melt temperature	250 – 285	°C
Nozzle temperature	235 – 275	°C
Front Section Zone 3 Temperature	235 – 285	°C
Temperature in Zone 2 of the middle section	235 – 285	°C
Temperature in Zone 1 of the rear section	225 – 245	°C
Mold temperature	60 – 90	°C
Hopper temperature	60 – 80	°C

Notes
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.