CYCOLOY™ C1200 resin

About
PC+ ABS，优异的冲击/耐高温。低温延性。用于汽车、电器和电器部件

Product Description
Supplier	SABIC
Generic	PC+ABS
Material Status	Commercial: Active
Features	High impact resistance,High Heat Resistance,Low temperature ductility
Availabilitys	North America

Technical Data
MECHANICAL	Nominal value	Unit	Test method
tensile strength
Yield, 50 mm/min	61	MPa	ASTM D638
Tensile strain
Yield, 50 mm/min	5	%	ASTM D638
Fracture, 50 mm/min	150	%	ASTM D638
Tensile modulus
50 mm/min	2320	MPa	ASTM D638
bending strength
Yield, 1.30 mm/min, 50 mm span	89	MPa	ASTM D790
Bending modulus
1.3 mm/min，50mm跨距	2390	MPa	ASTM D790

IMPACT	Nominal value	Unit	Test method
Impact strength of cantilever beam notch
23℃	650	J/m	ASTM D256
-30℃	540	J/m	ASTM D256
Total energy of instrument impact
23℃
23℃	63	J	ASTM D 3763
-30℃	63	J	ASTM D 3763

THERMAL	Nominal value	Unit	Test method
Vicat Softening Temp	130	℃	ISO 306
Hot deformation temperature
1.8 MPa, unannealed
3.2mm	129	℃	ASTM D 648
6.4mm	112	℃	ASTM D 648
Linear coefficient of thermal expansion
MD：-40~40℃	7.2E-05	1/℃	ASTM E 831
Relative temperature index
Electrical performance	105	℃	UL 746B
Impact mechanical performance	80	℃	UL 746B
Non mechanical impact performance	105	℃	UL 746B

PHYSICAL	Nominal value	Unit	Test method
Density	1.15		ASTM D792
Shrinkage rate
MD：3.2 mm	0.5- 0.7	%	Internal Method
Melt Flow Rate
260℃，5.0kg	11.4	g/10min	ASTM D1238

Electrical performance	Nominal value	Unit	Test method
Hot wire ignition {PLC	3	PLC Code	UL 746A
High current arc ignition (surface {PLC)	1	PLC Code	UL 746A
Compared to the leakage tracing index	2	PLC Code	UL 746A

FLAME CHARACTERISTICS	Nominal value	Unit	Test method
Flame retardant rating, 94HB flame rating evaluation	1.19	mm	UL 94

Process Conditions
injection molding	Nominal value	Unit	Test method
Drying temperature	105 – 110	°C
Drying time	3 – 4	hrs
Drying time (cumulative)	8	hrs
Maximum water content	0.04	%
Melt temperature	275 – 300	°C
Nozzle temperature	275 – 300	°C
Front Section Zone 3 Temperature	260 – 300	°C
Temperature in Zone 2 of the middle section	255 – 295	°C
Temperature in Zone 1 of the rear section	250 – 290	°C
Mold temperature	60 – 90	°C
Back pressure	0.3 – 0.7	MPa
Screw speed	40 – 70	rpm
Shoot to cylinder size	30 – 80	%
Depth of exhaust groove	0.038 – 0.076	mm

Notes
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.