| About |
|---|
| CYCOLOY C2950HF Polycarbonate/Acrylonitrile Butadiene Styrene (PC/ABS) resin is a high heat grade that can be injection molded. This non-chlorinated, non-brominated flame retardant high heat PC/ABS wih enhanced processability has a UL V0 & 5VA/B flame rating. CYCOLOY C2950HF resin is an excellent candidate for a wide variety of applications including appliances, lighting and electrical.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PC+ABS |
| Material Status | Commercial: Active |
| Features | High impact resistance,Good liquidity,Halogen free,Flame Characteristics,Heat Resistance, Good,V-2,V-0,5VA,5VB |
| Availabilitys | North America,Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.18 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 260℃，2.16kg | 22 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| TD：3.2 mm | 0.40 to 0.60 | % | Internal Method |
| MD：3.2 mm | 0.40 to 0.60 | % | Internal Method |
| Water absorption rate | |||
| Equilibrium, 23 ℃ | 0.40 | % | ASTM D570 |
| 24hr | 0.10 | % | ASTM D570 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 450 | J/m | ASTM D256 |
| Dart impact equipped with measuring instruments | |||
| 23℃，Energy at Peak Load | 54.2 | J | ASTM D3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 0.45 MPa, unannealed, 6.4 mm | 102 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 3.2 mm | 87.8 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 6.4 mm | 93.3 | ℃ | ASTM D648 |
| Vicat Softening Temp | 113 | ℃ | ASTM D1525 4 |
| Linear coefficient of thermal expansion | |||
| TD：-30~30℃ | 7.2E-5 | 1/℃ | ASTM D696 |
| MD：-30~30℃ | 7.2E-5 | 1/℃ | ASTM D696 |
| Thermal conductivity coefficient | 0.20 | W/m/K | ASTM C177 |
| Relative temperature index | |||
| Electrical performance | 85.0 | ℃ | UL 746 |
| Strength mechanical performance | 85.0 | ℃ | UL 746 |
| Impact mechanical performance | 85.0 | ℃ | UL 746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | > 1.0E+16 | ohms | ASTM D257 |
| Volume resistivity | 1.6E+17 | ohms·cm | ASTM D257 |
| Dielectric strength | |||
| 3.2 mm in oil | 24 | kV/mm | ASTM D149 |
| Dielectric constant | ASTM D150 | ||
| 50 Hz | 2.80 | ASTM D150 | |
| 60 Hz | 2.80 | ASTM D150 | |
| 1 MHz | 2.70 | ASTM D150 | |
| Dissipation factor | ASTM D150 | ||
| 50 Hz | 5.2E-3 | ASTM D150 | |
| 60 Hz | 5.2E-3 | ASTM D150 | |
| 1 MHz | 7.1E-3 | ASTM D150 | |
| Arc resistance | PLC 6 | ASTM D495 | |
| Compared to the leakage tracing index | PLC 2 | UL 746 | |
| High Arc Burning Index (HAI) | PLC 0 | UL 746 | |
| High voltage arc marking rate | |||
| HVTR | PLC 3 | UL 746 | |
| Hot wire ignition | |||
| HWI | PLC 2 | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 0.76 mm | V-2 | UL 94 | |
| 1.50 mm | V-0 | UL 94 | |
| 2.50 mm | 5VB | UL 94 | |
| 3.40 mm | 5VA | UL 94 | |
| Extreme oxygen index | 30 | % | ASTM D2863 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| yield | 64.1 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 40 | % | ASTM D638 |
| yield | 5.0 | % | ASTM D638 |
| Bending modulus | |||
| 100 mm span | 2590 | MPa | ASTM D790 |
| bending strength | |||
| Yield, 100 mm span | 96.5 | MPa | ASTM D790 |
| Rockwell hardness | |||
| R-level | 121 | ASTM D785 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 82 to 88 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Drying time, maximum | 8.0 | hr | |
| Recommended maximum moisture content | 0.040 | % | |
| Recommended injection volume | 30 to 80 | % | |
| Barrel rear temperature | 221 to 254 | °C | |
| Barrel middle temperature | 221 to 266 | °C | |
| Barrel front temperature | 243 to 277 | °C | |
| Nozzle temperature | 243 to 277 | °C | |
| Processing (melt) temperature | 243 to 277 | °C | |
| Mold temperature | 60 to 82 | °C | |
| Back pressure | 0.345 to 0.689 | MPa | |
| Screw speed | 40 to 70 | rpm | |
| Vent depth | 0.038 to 0.076 | mm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Type I, 2.0 in/min |
| 3. 0.10 in/min |
| 4. Rate A (50°C/h), Loading 2 (50 N) |
| 5. Tungsten Electrode |
| 6. Surface |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |