CYCOLOY™ CE1821 resin

About
高强度PC / ABS混合料具有高冲击、高热量、低线性膨胀系数、良好的表面质量和优异的挤出和热成型特性

Product Description
Supplier	SABIC
Generic	PC+ABS
Material Status	Commercial: Active
Features	Good surface appearance,High impact resistance
Availabilitys	North America

Technical Data
MECHANICAL	Nominal value	Unit	Test method
tensile strength
Yield, 5 mm/min	60	MPa	ISO 527
Fracture, 5 mm/min	55	MPa	ISO 527
Tensile strain
Yield, 5 mm/min	5	%	ISO 527
Fracture, 5 mm/min	110	%	ISO 527
Tensile modulus
1 mm/min	3100	MPa	ISO 527
bending strength
Yield, 2 mm/min	95	MPa	ISO 178
Bending modulus
2 mm/mim	3000	MPa	ISO 178

IMPACT	Nominal value	Unit	Test method
Impact strength of cantilever beam notch
23℃	500	J/m	ASTM D256
-30℃	120	J/m	ASTM D256
Impact strength of cantilever beam notch
23℃，80103	45	kJ/m²	ISO 180-1A
-30℃，80103	10	kJ/m²	ISO 180-1A
Charpy Notched Impact Strength
80103
23℃	40	kJ/m²	ISO 179/1eA
-30℃	10	kJ/m²	ISO 179/1eA
Total energy of instrument impact
23℃	66	J	仪表冲击总能量，23°C

THERMAL	Nominal value	Unit	Test method
Vicat Softening Temp	138	℃	ASTM D1525
Hot deformation temperature
1.8 MPa, 100 mm span	120	℃	ISO 75/Af
1.8 MPa, unannealed, 3.2 mm	120	℃	ASTM D648
Linear expansion coefficient, -40 ℃ to 40 ℃
flow	6.E-05	1/℃	ASTM E 831
transverse	7.E-05	1/℃	ASTM E 831
Thermal conductivity coefficient	0.2	W/m/℃	ISO 8302
Linear expansion coefficient, -40 ℃ to 40 ℃
flow	6.E-05	1/℃	ISO 11359-2
transverse	7.E-05	1/℃	ISO 11359-2
Ball pressure test
125℃±2℃	PASSES		IEC 60695-10-2
Vicat Softening Temp
B50	138	℃	ISO 306
B120	140	℃	ISO 306

PHYSICAL	Nominal value	Unit	Test method
Shrinkage rate
MD：3.2 mm	0.5 – 0.7	%	Internal Method
Melt Flow Rate
260℃，5.0kg	12	g/10min	ASTM D1238
Density	1.22	g/cm³	ISO 1183
Water absorption rate
Saturation, 23 ℃	0.4	%	ISO 62
23℃，50% RH	0.1	%	ISO 62
Melt Volume Rate
260℃，5 kg	10	cm³/10min	ISO 1133
Density	1.22		ASTM D792

Process Conditions
Sheet extrusion	Nominal value	Unit	Test method
injection molding	Nominal value	Unit	Test method
Drying temperature	110 – 120	°C
Drying time	3 – 4	hrs
Drying time (cumulative)	8	hrs
Maximum water content	0.04	%
Melt temperature	250 – 270	°C
Barrel Zone 3 Temperature	195 – 205	°C
Barrel Zone 3 Temperature	200 – 220	°C
Barrel Zone 3 Temperature	220 – 240	°C
Barrel Zone 3 Temperature	230 – 260	°C
The temperature of the adapter	230 – 260	°C
Core temperature	230 – 245	°C
Roller temperature – top	100 – 110	°C
Roller temperature – middle	110 – 120	°C
Roller temperature – lower part	145 – 155	°C
Drying temperature	110 – 120	°C
Drying time	2 – 6	hrs
Maximum water content	0.04	%
Melt temperature	270 – 300	°C
Nozzle temperature	260 – 290	°C
Front Zone 1 Temperature	270 – 300	°C
Temperature in Zone 2 of the middle section	265 – 290	°C
Temperature in Zone 3 of the rear section	260 – 270	°C
Mold temperature	60 – 100	°C
Back pressure	0.3 – 0.7	MPa
Screw speed	40 – 70	rpm
Shoot to cylinder size	30 – 80	%
Depth of exhaust groove	0.038 – 0.076	mm

Notes
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.