CYCOLOY™ CE3500 resin

About
CYCOLOY™ CE3500是吹塑/挤压等级，可提供低温延展性、高耐温性和高熔点

Product Description
Supplier	SABIC
Generic	PC+ABS
Material Status	Commercial: Active
Features	High Heat Resistance,Low temperature ductility
Availabilitys	Africa & Middle East ,Asia Pacific,Europe

Technical Data
MECHANICAL	Nominal value	Unit	Test method
Rockwell hardness
R-level	104		ISO 2039-2
tensile strength
Yield, 50 mm/min	50	MPa	ISO 527
Fracture, 50 mm/min	45	MPa	ISO 527
Tensile strain
Yield, 50 mm/min	5	%	ISO 527
Fracture, 50 mm/min	>70	%	ISO 527
Tensile modulus
1 mm/min	2000	MPa	ISO 527
bending strength
Yield, 2 mm/min	75	MPa	ISO 178
Bending modulus
2 mm/mim	1900	MPa	ISO 178
tensile strength
Yield, 5 mm/min	45	MPa	ISO 178
Fracture, 5 mm/min	45	MPa	ISO 178
Tensile strain
Yield, 5 mm/min	5	%	ISO 178
Fracture, 5 mm/min	>80	%	ISO 178

IMPACT	Nominal value	Unit	Test method
Impact strength of cantilever beam notch
23℃，80104	50	kJ/m²	ISO 180-1A
80104 -30℃	40	kJ/m²	ISO 180-1A
Impact strength of cantilever beam notch
23℃，80103	50	kJ/m²	ISO 180-1A
-30℃，80103	40	kJ/m²	ISO 180-1A
Charpy Notched Impact Strength
80 * 10 * 3, 62mm span
23℃	50	kJ/m²	ISO 179/1eA
-30℃	40	kJ/m²	ISO 179/1eA

THERMAL	Nominal value	Unit	Test method
Thermal conductivity coefficient	0.2	W/m/℃	ISO 8302
Linear expansion coefficient, -40 ℃ to 40 ℃
flow	8.E-05	1/℃	ISO 11359-2
transverse	8.E-05	1/℃	ISO 11359-2
Ball pressure test			IEC 60695-10-2
125℃±2℃	PASSES		IEC 60695-10-2
Maximum approximation value	125		IEC 60695-10-2
Vicat Softening Temp
B50	134	℃	ISO 306
B120	136	℃	ISO 306
Hot deformation temperature
0.45 MPa, 100 mm span	129	℃	ISO 75/Be
1.8 MPa, 100 mm span	110	℃	ISO 75/Ae

PHYSICAL	Nominal value	Unit	Test method
Shrinkage rate
MD：3.2 mm	0.5 – 0.7	%	Internal Method
Melt Flow Rate
260℃，5.0kg	2	g/10min	ASTM D1238
Density	1.15	g/cm³	ISO 1183
Water absorption rate
Saturation, 23 ℃	0.6	%	ISO 62
23℃，50% RH	0.2	%	ISO 62

Electrical performance	Nominal value	Unit	Test method
Dielectric strength
In oil
0.8 mm	40	kV/mm	IEC 60243-1
1.6mm	28	kV/mm	IEC 60243-1
3.2 mm	17	kV/mm	IEC 60243-1
Volume resistivity	> 1.E+15	ohms·cm	ASTM D257
Surface resistivity	> 1.0E+15	ohms/sq	ASTM D257

FLAME CHARACTERISTICS	Nominal value	Unit	Test method
94HB flame rating assessment	1.6	mm	UL 94
Extreme oxygen index
LOI	25	%	ISO 4589
Glowing wire flammability index
650 ℃, passed through	1	mm	IEC 60695-2-12

Process Conditions
injection molding	Nominal value	Unit	Test method
Drying temperature	100 – 110	°C
Drying time	2 – 4	hrs
Melt temperature (billet)	260 – 290	°C
Hopper temperature	240 – 280	°C
Temperature of barrel zone 1	210 – 230	°C
Temperature of barrel zone 2	240 – 260	°C
Barrel Zone 3 Temperature	240 – 260	°C
Accumulator temperature	240 – 260	°C
Mold temperature	50 – 70	°C
Core temperature	220 – 240	°C

Notes
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.