| About |
|---|
| CYCOLOY EXCY0372 is a 20% glass reinforced PC+ABS blend for injection molding purposes, featuring of balanced properties of high modulus, good flow and ductility. It is of Br- & Cl-free flame retardant systems.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PC+ABS |
| Material Status | Commercial: Active |
| Features | Ductility,Good liquidity,Halogen free,Flame Characteristics,V-1 |
| Availabilitys | Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Melt Volume Rate | |||
| 260℃，2.16 kg | 12.0 | cm³/10min | ISO 1133 |
| Water absorption rate | |||
| Saturation, 23 ℃ | 0.15 | % | ISO 62 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 80 | J/m | ASTM D256 |
| -30℃ | 9.0 | kJ/m² | ISO 180-1A |
| 23℃ | 9.0 | kJ/m² | ISO 180-1A |
| Notched impact strength of cantilever beam | |||
| 23℃ | 31 | kJ/m² | ISO 180/1U |
| Multi axial instrumented impact energy | 11.0 | J | ISO 6603-2 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 0.45 MPa, unannealed, 3.2 mm | 90.0 | ℃ | |
| 1.8 MPa, unannealed, 3.2 mm | 94.0 | ℃ | |
| Vicat Softening Temp | |||
| — | 93.0 | ℃ | ASTM D1525 7 |
| B120 | 98.0 | ℃ | ISO 306/B120 |
| Linear coefficient of thermal expansion | ASTM E831 | ||
| MD：-40~40℃ | 2.0E-5 | 1/℃ | |
| TD：-40~40℃ | 5.0E-5 | 1/℃ | |
| Thermal conductivity coefficient | |||
| 50℃ | 0.20 | W/m/K | ASTM C177 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 3.00 mm | V-1 | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 115 | ISO 2039-2 | |
| Tensile modulus | 7000 | MPa | ASTM D638 |
| tensile strength | |||
| fracture | 100 | MPa | ISO 527-2/5 |
| Tensile strain | |||
| fracture | 3.0 | % | ISO 527-2/5 |
| Bending modulus | 6700 | MPa | ISO 178 |
| bending strength | 150 | MPa | ISO 178 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80.0 to 90.0 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.010 | % | |
| Barrel rear temperature | 230 to 270 | °C | |
| Barrel middle temperature | 240 to 280 | °C | |
| Barrel front temperature | 250 to 280 | °C | |
| Nozzle temperature | 250 to 280 | °C | |
| Processing (melt) temperature | 250 to 280 | °C | |
| Mold temperature | 80.0 to 100 | °C | |
| Back pressure | 3.00 to 9.00 | MPa | |
| Screw speed | 30 to 150 | rpm | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |