| About |
|---|
| CYCOLOY™ CM6140 resin CYCOLOY resin grade CM6140 is a flame retardant, filled PC/ABS blend. It is of non-brominated & non-chlorinated FR system to meet UL94 V0 at 0.8mm. Key features include thin wall FR, higher stiffness, balanced properties in flow, impact and heat designed for various thin wall applications.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PC+ABS |
| Material Status | Commercial: Active |
| Features | Good Rigidity,High impact resistance,Good liquidity,Halogen free,Flame Characteristics,Heat Resistance, Good,V-1,V-0,5VB |
| Availabilitys | North America,Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | |||
| — | 1.26 | g/cm³ | ASTM D792 |
| — | 1.25 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 260℃，2.16kg | 18 | g/10min | ASTM D1238 |
| Melt Volume Rate | |||
| 220℃，5 kg | 14.0 | cm³/10min | ISO 1133 |
| Shrinkage rate | Internal Method | ||
| MD：3.2 mm | 0.30 to 0.50 | % | |
| TD：3.2 mm | 0.40 to 0.60 | % | |
| Water absorption rate | |||
| 24hr，50% RH | 0.010 | % | ASTM D570 |
| 24hr | 0.10 | % | ASTM D570 |
| Saturation, 23 ℃ | 0.090 | % | ISO 62 |
| Equilibrium, 23 ℃, 50% RH | 0.010 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| — | 3500 | MPa | ASTM D638 |
| — | 3200 | MPa | ISO 527-1-2 |
| tensile strength | |||
| yield | 65.0 | MPa | ASTM D638 |
| yield | 65.0 | MPa | ASTM D638 |
| fracture | 50.0 | MPa | ASTM D638 |
| fracture | 50.0 | MPa | ISO 527-2/5 |
| Tensile strain | |||
| yield | 4.0 | % | ASTM D638 |
| yield | 3.5 | % | ISO 527-2/5 |
| fracture | 100 | % | ASTM D638 |
| fracture | 15 | % | ISO 527-2/50 |
| Bending modulus | |||
| 50 mm span | 3300 | MPa | ASTM D790 |
| — | 3450 | MPa | ISO 178 |
| bending strength | |||
| — | 97.0 | MPa | ISO 178 |
| Yield, 50 mm span | 100 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30℃ | 5.0 | kJ/m² | |
| 23℃ | 10 | kJ/m² | |
| Impact strength of cantilever beam notch | |||
| -30℃ | 88 | J/m | ASTM D256 |
| 23℃ | 200 | J/m | ASTM D256 |
| -30℃ | 5.0 | kJ/m² | ISO 180-1A |
| 23℃ | 10 | kJ/m² | ISO 180-1A |
| Dart impact equipped with measuring instruments | |||
| 23℃，Total Energy | 50.0 | J | ASTM D3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed, 6.4 mm | 97.0 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 3.2 mm | 83.0 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 6.4 mm | 89.0 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 64 mm span | 80.0 | ℃ | ISO 75-2/Af |
| Vicat Softening Temp | |||
| — | 91.0 | ℃ | ASTM D1525 15 |
| B50 | 98.0 | ℃ | ISO 306 |
| B120 | 102 | ℃ | ISO 306/B120 |
| Ball pressure test | |||
| 75℃ | Pass | IEC 60695-10-2 | |
| Linear coefficient of thermal expansion | ASTM E831, ISO 11359-2 | ||
| MD：-40~40℃ | 5.5E-5 | 1/℃ | |
| TD：-40~40℃ | 6.0E-5 | 1/℃ |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 3.5E+15 | ohms | ASTM D257 |
| Volume resistivity | 2.7E+16 | ohms·cm | ASTM D257 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 0.60 mm | V-1 | ||
| 0.80 mm | V-0 | ||
| 1.50 mm | 5VB | ||
| Glowing wire flammability index | |||
| 0.80 mm | 960 | ℃ | IEC 60695-2-12 |
| Igniting temperature of the hot wire | IEC 60695-2-13 | ||
| 1 mm | 850 | ℃ | |
| 3 mm | 800 | ℃ |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 90.0 | °C | |
| Drying time | > 4.0 | hr | |
| Recommended maximum moisture content | 0.040 | % | |
| Barrel rear temperature | 275 to 300 | °C | |
| Barrel middle temperature | 275 to 300 | °C | |
| Barrel front temperature | 280 to 300 | °C | |
| Nozzle temperature | 280 to 300 | °C | |
| Processing (melt) temperature | 275 to 300 | °C | |
| Mold temperature | 60.0 to 80.0 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |