| About |
|---|
| CYCOLOY CM6210 Polycarbonate/Acrylonitrile Butadiene Styrene (PC/ABS) resin is a mineral filled, low warpage grade that can be injection molded or extruded into sheet for secondary thermoforming operations. This non-chlorinated, non-brominated flame retardant PC/ABS has a UL V0 flame rating. CYCOLOY CM6210 resin is an excellent candidate for a wide variety of applications including enclosures.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PC+ABS |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Halogen free,Flame Characteristics,V-0 |
| Availabilitys | North America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.28 | g/cm³ | ASTM D792 |
| Density | 1.27 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 260℃，5.0kg | 12 | g/10min | ASTM D1238 |
| Melt Volume Rate | |||
| 260℃，5 kg | 9.00 | cm³/10min | ISO 1133 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.40 to 0.60 | % | Internal Method |
| Water absorption rate | |||
| Saturation, 23 ℃ | 0.30 | % | ISO 62 |
| Equilibrium, 23 ℃, 50% RH | 0.10 | % | ISO 62 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30℃ | 10 | kJ/m² | ISO 179/1eA |
| 23℃ | 45 | kJ/m² | ISO 179/1eA |
| Impact strength of cantilever beam notch | ASTM D256 | ||
| -30℃ | 90 | J/m | ASTM D256 |
| 23℃ | 500 | J/m | ASTM D256 |
| Impact strength of cantilever beam notch | ISO 180/1A | ||
| -30℃ | 10 | kJ/m² | ISO 180-1A |
| 23℃ | 45 | kJ/m² | ISO 180-1A |
| Dart impact equipped with measuring instruments | |||
| 23℃，Total Energy | 45.0 | J | ASTM D3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 3.2 mm | 90.0 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 100 mm span | 89.0 | ℃ | ISO 75-2/Ae |
| 0.45 MPa, unannealed, 100 mm span | 99.0 | ℃ | ISO 75-2/Be |
| Vicat Softening Temp | 106 | ℃ | ASTM D1525 10 |
| Vicat Softening Temp | |||
| B50 | 112 | ℃ | ISO 306 |
| B120 | 114 | ℃ | ISO 306/B120 |
| Ball pressure test | IEC 60695-10-2 | ||
| 75℃ | Pass | IEC 60695-10-2 | |
| 95℃ | Pass | IEC 60695-10-2 | |
| Linear coefficient of thermal expansion | |||
| TD：-40~40℃ | 7.0E-5 | 1/℃ | ASTM E831 |
| TD | ISO 11359-2 | ||
| MD：-40~40℃ | 5.7E-5 | 1/℃ | ASTM E831 |
| MD | ISO 11359-2 | ||
| -40 to 40 ℃ | 5.2E-5 | cm/cm/℃ | ISO 11359-2 |
| 23 to 60 ℃ | 5.2E-5 | cm/cm/℃ | ISO 11359-2 |
| -40 to 40 ℃ | 6.0E-5 | cm/cm/℃ | ISO 11359-2 |
| 23 to 60 ℃ | 6.0E-5 | cm/cm/℃ | ISO 11359-2 |
| Thermal conductivity coefficient | 0.30 | W/m/K | ISO 8302 |
| Relative temperature index | |||
| Electrical performance | 60.0 | ℃ | UL 746 |
| Strength mechanical performance | 60.0 | ℃ | UL 746 |
| Impact mechanical performance | 60.0 | ℃ | UL 746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Dielectric strength | IEC 60243-1 | ||
| 0.8 mm in oil | 38 | kV/mm | IEC 60243-1 |
| 1.6 mm in oil | 26 | kV/mm | IEC 60243-1 |
| 3.2 mm in oil | 17 | kV/mm | IEC 60243-1 |
| Relative permittivity | IEC 60250 | ||
| 50 Hz | 2.90 | IEC 60250 | |
| 60 Hz | 2.90 | IEC 60250 | |
| 1 MHz | 2.80 | IEC 60250 | |
| Dissipation factor | IEC 60250 | ||
| 50 Hz | 3.0E-3 | IEC 60250 | |
| 60 Hz | 3.0E-3 | IEC 60250 | |
| 1 MHz | 4.0E-3 | IEC 60250 | |
| Compared to the leakage tracing index | 250 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.50 mm | V-0 | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 3570 | MPa | ASTM D638 |
| Tensile modulus | 3660 | MPa | ISO 527-1-2 |
| tensile strength | |||
| fracture | 50.0 | MPa | ASTM D638 |
| yield | 64.0 | MPa | ASTM D638 |
| yield | 59.7 | MPa | ISO 527-2/5 |
| yield | 63.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| fracture | 80 | % | ASTM D638 |
| yield | 4.9 | % | ASTM D638 |
| yield | 3.6 | % | ISO 527-2/5 |
| yield | 3.5 | % | ISO 527-2/50 |
| Bending modulus | 3560 | MPa | ISO 178 |
| 50 mm span | 3500 | MPa | ASTM D790 |
| bending strength | 106 | MPa | ISO 178 |
| bending strength | |||
| Yield, 50 mm span | 110 | MPa | ASTM D790 |
| Rockwell hardness | |||
| R-level | 98 | ISO 2039-2 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Drying temperature | 82 to 88 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Barrel 1 zone temperature | 182 to 227 | °C | |
| Barrel 2 zone temperature | 188 to 232 | °C | |
| Barrel 3 zone temperature | 204 to 241 | °C | |
| Barrel 4 zone temperature | 210 to 243 | °C | |
| Connector temperature | 210 to 243 | °C | |
| Melt temperature | 221 to 243 | °C | |
| Nozzle temperature | 210 to 243 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.20 in/min |
| 3. Type I, 0.20 in/min |
| 4. 0.051 in/min |
| 5. 0.079 in/min |
| 6. at Yield |
| 7. 80*10*3 sp=62mm |
| 8. 80*10*3 mm |
| 9. 120*10*4 mm |
| 10. Rate A (50°C/h), Loading 2 (50 N) |
| 11. Approximate Maximum |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |