About |
---|
高热量,用于汽车电镀应用,良好的平衡流动性/冲击性能 |
Product Description | |
---|---|
Supplier | SABIC |
Generic | PC+ABS |
Material Status | Commercial: Active |
Features | Good liquidity |
Availabilitys | North America |
Technical Data | |||
---|---|---|---|
MECHANICAL | Nominal value | Unit | Test method |
tensile strength | |||
Yield, 50 mm/min | 68 | MPa | ISO 527 |
Fracture, 50 mm/min | 40 | MPa | ISO 527 |
Tensile strain | |||
Yield, 50 mm/min | 3.8 | % | ISO 527 |
Fracture, 50 mm/min | 15 | % | ISO 527 |
Tensile modulus | |||
1 mm/min | 2750 | MPa | ISO 527 |
bending strength | |||
Yield, 2 mm/min | 100 | MPa | ISO 178 |
Bending modulus | |||
2 mm/mim | 2650 | MPa | ISO 178 |
IMPACT | Nominal value | Unit | Test method |
---|---|---|---|
Impact strength of cantilever beam notch | |||
23℃ | 70 | J/m | ASTM D256 |
-30℃ | 50 | J/m | ASTM D256 |
Total energy of instrument impact | |||
23℃ | 41 | J | ASTM D 3763 |
Impact strength of cantilever beam notch | |||
23℃,80*10*3 | 10 | kJ/m² | ISO 180-1A |
-30℃,80*10*3 | 5 | kJ/m² | ISO 180-1A |
Charpy Notched Impact Strength | |||
80*10*3 | |||
23℃ | 10 | kJ/m² | ISO 179/1eA |
-30℃ | 5 | kJ/m² | ISO 179/1eA |
THERMAL | Nominal value | Unit | Test method |
---|---|---|---|
Vicat Softening Temp | 91 | ℃ | ASTM D1525 |
Hot deformation temperature | |||
1.8 MPa, 64 mm span | 77 | ℃ | ISO 75/Af |
1.8 MPa, unannealed, 3.2 mm | ℃ | ASTM D648 | |
Linear expansion coefficient, -40 ℃ to 40 ℃ | |||
flow | 6.E-05 | 1/℃ | ASTM E 831 |
transverse | 6.E-05 | 1/℃ | ASTM E 831 |
Linear expansion coefficient, -40 ℃ to 40 ℃ | |||
flow | 7.5E-05 | 1/℃ | ISO 11359-2 |
transverse | 7.5E-05 | 1/℃ | ISO 11359-2 |
Ball pressure test | |||
75℃±2℃ | PASSES | IEC 60695-10-2 | |
Vicat Softening Temp | |||
B50 | 90 | ℃ | ISO 306 |
B120 | 95 | ℃ | ISO 306 |
PHYSICAL | Nominal value | Unit | Test method |
---|---|---|---|
Density | 1.18 | ASTM D792 | |
Shrinkage rate | SABIC Method | ||
MD:3.2 mm | % | Internal Method | |
TD:3.2 mm | % | Internal Method | |
Melt Flow Rate | |||
260℃,5.0kg | 22 | g/10min | ASTM D1238 |
Density | 1.18 | g/cm³ | ISO 1183 |
Water absorption rate | |||
Saturation, 23 ℃ | 0.2 | % | ISO 62 |
23℃,50% RH | 0.1 | % | ISO 62 |
Melt Volume Rate | |||
260℃,5 kg | 18 | cm³/10min | ISO 1133 |
Process Conditions | |||
---|---|---|---|
injection molding | Nominal value | Unit | Test method |
Drying temperature | 100 – 105 | °C | |
Drying time | 3 – 4 | hrs | |
Drying time (cumulative) | 8 | hrs | |
Maximum water content | 0.04 | % | |
Melt temperature | 260 – 290 | °C | |
Nozzle temperature | 260 – 290 | °C | |
Front Section Zone 3 Temperature | 255 – 290 | °C | |
Temperature in Zone 2 of the middle section | 255 – 290 | °C | |
Temperature in Zone 1 of the rear section | 250 – 280 | °C | |
Mold temperature | 70 – 100 | °C | |
Back pressure | 0.3 – 0.7 | MPa | |
Screw speed | 40 – 70 | rpm | |
Shoot to cylinder size | 30 – 80 | % | |
Depth of exhaust groove | 0.038 – 0.076 | mm |
Notes |
---|
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |