CYCOLOY™ CU1650 resin

About
UV稳定，非溴化和非氯化阻燃系统的 PC/ABS，良好流动和冲击性能

Product Description
Supplier	SABIC
Generic	PC+ABS
Material Status	Commercial: Active
Features	Weather resistance is good,Good liquidity,Halogen free
Availabilitys	North America

Technical Data
MECHANICAL	Nominal value	Unit	Test method
tensile strength
Yield, 50 mm/min	54	MPa	ISO 527
Fracture, 50 mm/min	53	MPa	ISO 527
Tensile strain
Yield, 50 mm/min	4.5	%	ISO 527
Fracture, 50 mm/min	120	%	ISO 527
Tensile modulus
1 mm/min	2250	MPa	ISO 527
bending strength
Yield, 2 mm/min	80	MPa	ISO 178
Bending modulus
2 mm/mim	2200	MPa	ISO 178

IMPACT	Nominal value	Unit	Test method
Impact strength of cantilever beam notch
23℃	600	J/m	ASTM D256
-30℃	400	J/m	ASTM D256
Total energy of instrument impact
23℃	56	J	ASTM D 3763
Impact strength of cantilever beam notch
23℃，80103	65	kJ/m²	ISO 180-1A
-30℃，80103	30	kJ/m²	ISO 180-1A
Charpy Notched Impact Strength
80 * 10 * 3, 62mm span
23℃	65	kJ/m²	ISO 179/1eA
-30℃	30	kJ/m²	ISO 179/1eA

THERMAL	Nominal value	Unit	Test method
Vicat Softening Temp	126	℃	ASTM D1525
Hot deformation temperature
1.8 MPa, 64 mm span	126	℃	ISO 75/Bf
1.8 MPa, 64 mm span	105	℃	ISO 75/Af
1.8 MPa, unannealed, 3.2 mm	107	℃	ASTM D648
Linear expansion coefficient, -40 ℃ to 40 ℃
flow	7.E-05	1/℃	ASTM E 831
transverse	7.E-05	1/℃	ASTM E 831
Thermal conductivity coefficient	0.2	W/m/℃	ISO 8302
Linear expansion coefficient, -40 ℃ to 40 ℃
flow	8.E-05	1/℃	ISO 11359-2
transverse	8.E-05	1/℃	ISO 11359-2
Ball pressure test
75℃±2℃	PASSES		IEC 60695-10-2
Vicat Softening Temp
B50	126	℃	ISO 306
B120	127	℃	ISO 306
Relative temperature index
Electrical performance	60	℃	UL 746B
Impact mechanical performance	60	℃	UL 746B
Non mechanical impact performance	60	℃	UL 746B

PHYSICAL	Nominal value	Unit	Test method
Density	1.14		ASTM D792
Shrinkage rate
MD：3.2 mm	0.5 – 0.7	%	Internal Method
TD：3.2 mm	0.5 – 0.7	%	Internal Method
Melt Flow Rate
260℃，5.0kg	28	g/10min	ASTM D1238
Density	1.14	g/cm³	ISO 1183
Water absorption rate
Saturation, 23 ℃	0.4	%	ISO 62
23℃，50% RH	0.15	%	ISO 62
Melt Volume Rate
260℃，2.16 kg	8	cm³/10min	ISO 1133
260℃，5 kg	25	cm³/10min	ISO 1133

Electrical performance	Nominal value	Unit	Test method
Dielectric strength
In oil			ASTM D149
0.8 mm	35	kV/mm	IEC 60243-1
1.6mm	25	kV/mm	IEC 60243-1
3.2 mm	17	kV/mm	IEC 60243-1
Volume resistivity	> 1.E+15	ohms·cm	IEC 60093
Surface resistivity	>1.0E+15		IEC 60093

FLAME CHARACTERISTICS	Nominal value	Unit	Test method
Igniting temperature of the hot wire
1.5 mm	750	℃	IEC 60695-2-13

Process Conditions
injection molding	Nominal value	Unit	Test method
Drying temperature	95 – 105	°C
Drying time	2 – 4	hrs
Maximum water content	0.02	%
Melt temperature	260 – 290	°C
Nozzle temperature	240 – 280	°C
Front Section Zone 3 Temperature	260 – 290	°C
Temperature in Zone 2 of the middle section	250 – 290	°C
Temperature in Zone 1 of the rear section	230 – 260	°C
Mold temperature	60 – 80	°C
Hopper temperature	60 – 90	°C

Notes
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.