CYCOLOY™ CX5430 resin

About
CYCOLOY™ CX5430是一种普通用途的PC / ABS混合材料，适用于要求焊缝强度、高流动性和冲击性的薄壁应用，并具有良好的其他性能平衡。

Product Description
Supplier	SABIC
Generic	PC+ABS
Material Status	Commercial: Active
Features	Good Rigidity,High liquidity
Availabilitys	Africa & Middle East ,Asia Pacific,Europe

Technical Data
MECHANICAL	Nominal value	Unit	Test method
Rockwell hardness
Level L	90		ISO 2039-2
R-level	115		ISO 2039-2
Taber wear and tear
CS-17，1kg	70	mg/1000cy	Internal Method
tensile strength
Yield, 50 mm/min	48	MPa	ISO 527
Fracture, 50 mm/min	44	MPa	ISO 527
Tensile strain
Yield, 50 mm/min	5	%	ISO 527
Fracture, 50 mm/min	>50	%	ISO 527
Tensile modulus
1 mm/min	2400	MPa	ISO 527
bending strength
Yield, 2 mm/min	75	MPa	ISO 178
Bending modulus	2300	MPa	ISO 178
2 mm/mim	900	MPa	ISO 178
tensile strength
Yield, 5 mm/min	44	MPa	ISO 178
Fracture, 5 mm/min	44	MPa	ISO 178
Tensile strain
Yield, 5 mm/min	5	%	ISO 178
Fracture, 5 mm/min	>50	%	ISO 178

IMPACT	Nominal value	Unit	Test method
Izod notched impact strength
Double barrier, 23 ℃	110	J/m	SABIC Method
Impact strength of cantilever beam notch
23℃	500	J/m	ASTM D256
-30℃	250	J/m	ASTM D256
Multiaxial impact	82	J	ISO 6603
Total energy of instrument impact
23℃	56	J	ASTM D 3763
-30℃	41	J	ASTM D 3763
Impact strength of cantilever beam notch
23℃，80103	40	kJ/m²	ISO 180-1A
-30℃，80103	20	kJ/m²	ISO 180-1A
Charpy Notched Impact Strength
80 * 10 * 3, 62mm span
23℃	40	kJ/m²	ISO 179/1eA
-30℃	20	kJ/m²	ISO 179/1eA

THERMAL	Nominal value	Unit	Test method
Vicat Softening Temp	115	℃	ASTM D1525
Hot deformation temperature
0.45 MPa, 100 mm span	117	℃	ISO 75/Be
1.8 MPa, 100 mm span	95	℃	ISO 75/Af
Unannealed, 3.2 mm
0.45 MPa	115	℃	ASTM D 648
1.8MPa	95	℃	ASTM D 648
Linear expansion coefficient, -40 ℃ to 40 ℃
flow	8.E-05	1/℃	ASTM E 831
transverse	8.E-05	1/℃	ASTM E 831
Thermal conductivity coefficient
	0.2	W/m/℃	ASTM C177
	0.2	W/m/℃	ISO 8302
Linear expansion coefficient, -40 ℃ to 40 ℃
flow	8.E-05	1/℃	ISO 11359-2
transverse	8.E-05	1/℃	ISO 11359-2
Ball pressure test			IEC 60695-10-2
125℃±2℃	PASSES		IEC 60695-10-2
Maximum approximation value	100		IEC 60695-10-2
Vicat Softening Temp
B50	114	℃	ISO 306
B120	115	℃	ISO 306
Relative temperature index
Electrical performance	60	℃	UL 746B
Impact mechanical performance	60	℃	UL 746B
Non mechanical impact performance	60	℃	UL 746B

PHYSICAL	Nominal value	Unit	Test method
Density	1.15		ASTM D 792
mould	1.15	g/cm³	ISO 1133
Shrinkage rate
MD：3.2 mm	0.5 – 0.7	%	Internal Method
Melt Flow Rate
260℃，5.0kg	19	g/10min	ASTM D1238
Density	1.15	g/cm³	ISO 1183
Water absorption rate
Saturation, 23 ℃	0.3	%	ISO 62
23℃，50% RH	0.07	%	ISO 62
Melt Volume Rate
260℃，5 kg	18	cm³/10min	ISO 1133

Electrical performance	Nominal value	Unit	Test method
Dielectric strength
In oil			ASTM D149
0.8 mm	35	kV/mm	IEC 60243-1
1.5mm	25	kV/mm	IEC 60243-1
Relative permittivity
50-60 Hz	2.9		IEC 60250
1 kHz	2.7		IEC 60250
Dissipation factor
50-60 Hz	0.01		IEC 60250
1 MHz	0.011		IEC 60250
Volume resistivity	> 1.E+15	ohms·cm	ASTM D257
Surface resistivity	> 1.0E+15	ohms/sq	ASTM D257

FLAME CHARACTERISTICS	Nominal value	Unit	Test method
94HB flame rating assessment	1.5	mm	UL 94
94HB flame rating evaluation second reference value	3	mm	UL 94
Glowing wire flammability index
650 ℃, passed through	3.2	mm	IEC 60695-2-12

Process Conditions
injection molding	Nominal value	Unit	Test method
Drying temperature	100 – 110	°C
Drying time	2 – 4	hrs
Maximum water content	0.02	%
Melt temperature	260 – 290	°C
Nozzle temperature	240 – 280	°C
Front Section Zone 3 Temperature	250 – 290	°C
Temperature in Zone 2 of the middle section	250 – 290	°C
Temperature in Zone 1 of the rear section	230 – 260	°C
Mold temperature	60 – 90	°C
Hopper temperature	60 – 80	°C

Notes
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.