| CYCOLOY CX7211 Polycarbonate/Acrylonitrile Butadiene Styrene (PC/ABS) resin is an enhanced performance & processibility grade that can be injection molded. This non-chlorinated, non-brominated flame retardant PC/ABS has a UL V0 & 5VA/B flame rating. CYCOLOY CX7211 resin is an excellent candidate for a wide variety of thin wall applications including enclosures.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PC+ABS |
| Material Status | Commercial: Active |
| Features | High impact resistance,Good liquidity,Heat Resistance, Good,V-1,V-0,5VA,5VB |
| Availabilitys | North America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.18 | g/cm³ | ASTM D792 |
| Density | 1.19 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 260℃，2.16kg | 16 | g/10min | ASTM D1238 |
| Melt Volume Rate | |||
| 260℃，2.16 kg | 14.0 | cm³/10min | ISO 1133 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.40 to 0.60 | % | Internal Method |
| Water absorption rate | |||
| Saturation, 23 ℃ | 0.24 | % | ISO 62 |
| Equilibrium, 23 ℃, 50% RH | 0.12 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 2950 | MPa | ASTM D638 |
| Tensile modulus | 2800 | MPa | ISO 527-1-2 |
| tensile strength | |||
| fracture | 55.0 | MPa | ISO 527-2/50 |
| fracture | 60.0 | MPa | ASTM D638 |
| yield | 66.0 | MPa | ASTM D638 |
| yield | 62.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| fracture | 90 | % | ISO 527-2/50 |
| fracture | 98 | % | ASTM D638 |
| yield | 4.0 | % | ISO 527-2/50 |
| yield | 4.0 | % | ASTM D638 |
| Bending modulus | 2500 | MPa | ISO 178 |
| 50 mm span | 2750 | MPa | ASTM D790 |
| bending strength | 100 | MPa | ISO 178 |
| bending strength | |||
| Yield, 50 mm span | 103 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30℃ | 10 | kJ/m² | ISO 179/1eA |
| 23℃ | 40 | kJ/m² | ISO 179/1eA |
| Impact strength of cantilever beam notch | ASTM D256 | ||
| -30℃ | 130 | J/m | ASTM D256 |
| 23℃ | 630 | J/m | ASTM D256 |
| Impact strength of cantilever beam notch | ISO 180/1A | ||
| -30℃ | 10 | kJ/m² | ISO 180-1A |
| 23℃ | 40 | kJ/m² | ISO 180-1A |
| Dart impact equipped with measuring instruments | |||
| 23℃，Total Energy | 60.0 | J | ASTM D3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 1.8 MPa, unannealed, 64 mm span | 90.0 | ℃ | ISO 75-2/Af |
| 0.45 MPa, unannealed, 3.2 mm | 94.0 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed, 6.4 mm | 102 | ℃ | ASTM D648 |
| Hot deformation temperature | ASTM D648 | ||
| 1.8 MPa, unannealed, 3.2 mm | 89.0 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 6.4 mm | 96.0 | ℃ | ASTM D648 |
| Vicat Softening Temp | 105 | ℃ | ASTM D1525 10 |
| Vicat Softening Temp | |||
| B50 | 105 | ℃ | ISO 306 |
| B120 | 105 | ℃ | ISO 306/B120 |
| Ball pressure test | |||
| 75℃ | Pass | IEC 60695-10-2 | |
| Linear coefficient of thermal expansion | |||
| TD：-40~40℃ | 7.5E-5 | 1/℃ | ISO 11359-2 |
| TD：-40~40℃ | 5.5E-5 | 1/℃ | ASTM E831 |
| MD：-40~40℃ | 7.5E-5 | 1/℃ | ISO 11359-2 |
| MD：-40~40℃ | 6.1E-5 | 1/℃ | ASTM E831 |
| Thermal conductivity coefficient | 0.20 | W/m/K | ISO 8302 |
| Relative temperature index | |||
| Electrical performance | 90.0 | ℃ | UL 746 |
| Strength mechanical performance | 90.0 | ℃ | UL 746 |
| Impact mechanical performance | 90.0 | ℃ | UL 746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric strength | IEC 60243-1 | ||
| 0.8 mm in oil | 35 | kV/mm | IEC 60243-1 |
| 1.6 mm in oil | 25 | kV/mm | IEC 60243-1 |
| 3.2 mm in oil | 17 | kV/mm | IEC 60243-1 |
| Compared to the leakage tracing index | PLC 3 | UL 746 | |
| High Arc Burning Index (HAI) | PLC 0 | UL 746 | |
| Hot wire ignition | |||
| HWI | PLC 2 | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 1.30 mm | V-1 | UL 94 | |
| 1.50 mm | V-0 | UL 94 | |
| 2.00 mm | 5VB | UL 94 | |
| 2.50 mm | 5VA | UL 94 | |
| Glowing wire flammability index | |||
| 1.0 mm | 960 | ℃ | IEC 60695-2-12 |
| Igniting temperature of the hot wire | IEC 60695-2-13 | ||
| 1 mm | 800 | ℃ | IEC 60695-2-13 |
| 3 mm | 800 | ℃ | IEC 60695-2-13 |
| Extreme oxygen index | 32 | % | ISO 4589-2 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 82 to 88 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Drying time, maximum | 8.0 | hr | |
| Recommended maximum moisture content | 0.040 | % | |
| Recommended injection volume | 30 to 80 | % | |
| Barrel rear temperature | 221 to 254 | °C | |
| Barrel middle temperature | 221 to 266 | °C | |
| Barrel front temperature | 243 to 277 | °C | |
| Nozzle temperature | 243 to 277 | °C | |
| Processing (melt) temperature | 243 to 277 | °C | |
| Mold temperature | 60 to 82 | °C | |
| Back pressure | 0.345 to 0.689 | MPa | |
| Screw speed | 40 to 70 | rpm | |
| Vent depth | 0.038 to 0.076 | mm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.20 in/min |
| 3. Type I, 2.0 in/min |
| 4. 0.051 in/min |
| 5. 0.079 in/min |
| 6. at Yield |
| 7. 80*10*3 sp=62mm |
| 8. 80*10*3 mm |
| 9. 80*10*4 mm |
| 10. Rate A (50°C/h), Loading 2 (50 N) |
| 11. Surface |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |