CYCOLOY™ CY5100 resin

About
CYCOLOY™CY5100是聚碳酸酯(PC)和ABS混合的树脂。是一种非溴化和非氯化阻燃剂。无定形，经久耐用，具有良好的流动/冲击平衡和良好的加工能力。提供了高耐热性。采用注塑成型，适用于大型应用。

Product Description
Supplier	SABIC
Generic	PC+ABS
Material Status	Commercial: Active
Features	Excellent Processability,High Heat Resistance,Durability
Availabilitys	Asia Pacific

Technical Data
MECHANICAL	Nominal value	Unit	Test method
tensile strength
Fracture, Type I, 50 mm/min	47	MPa	ASTM D638
Fracture, 50 mm/min	46	MPa	ISO 527
Yield, Type I, 50 mm/min	63	MPa	ASTM D638
Yield, 5 mm/min	63	MPa	ISO 527
Tensile strain
Fracture, Type I, 50 mm/min	65	%	ASTM D638
Fracture, 50 mm/min	35	%	ISO 527
Yield, Type I, 50 mm/min	4.1	%	ASTM D638
Yield, 50 mm/min	4	%	ISO 527
Tensile modulus
5 mm/min	2760	MPa	ASTM D638
1 mm/min	2750	MPa	ISO 527
bending strength
Yield, 2 mm/min	94	MPa	ISO 527
Bending modulus
2 mm/mim	2440	MPa	ISO 527

IMPACT	Nominal value	Unit	Test method
Impact strength of cantilever beam notch
23℃	400	J/m	ASTM D256
Impact strength of cantilever beam notch
-30℃	80	J/m	ASTM D256
Impact strength of cantilever beam notch
23℃，80103	45	kJ/m²	ISO 180-1A
Impact strength of cantilever beam notch
-30℃，80103	10	kJ/m²	ISO 180-1A
Charpy Notched Impact Strength
23 ℃, 80 * 10 * 3, 62mm span	45	kJ/m²	ISO 179/1eA
-30 ℃, 80 * 10 * 3, 62mm span	10	kJ/m²	ISO 179/1eA

THERMAL	Nominal value	Unit	Test method
Linear coefficient of thermal expansion
MD：-30~40℃	8.E-05	1/℃	ISO 11359-2
Linear coefficient of thermal expansion
TD：-30~40℃	8.E-05	1/℃	ISO 11359-2
Ball pressure test
125℃±2℃	通过		IEC 60695-10-2
Vicat Softening Temp	104	℃	ISO 306
Vicat Softening Temp	106	℃	ISO 306
Hot deformation temperature
1.8 MPa, 64 mm span	88	℃	ISO 75/Af
Relative temperature index
Non mechanical impact performance	60	℃	UL 746B
Electrical performance	60	℃	UL 746B
Impact mechanical performance	60	℃	UL 746B

PHYSICAL	Nominal value	Unit	Test method
Shrinkage rate
MD：3.2 mm	0.4 – 0.6	%	Internal Method
Density	0.04		ISO 1183
Water absorption rate
23℃，50% RH	0.2	%	ISO 62
Saturation, 23 ℃	0.6	%	ISO 62
Melt Volume Rate
300℃，1.2 kg	23	cm³/10min	ISO 1133

Electrical performance	Nominal value	Unit	Test method
Hot wire ignition {PLC}	3	PLC Code	UL 746A
Compared to the leakage tracing index	2	PLC Code	UL 746A
Volume resistivity	1.E + 15	ohms·cm	IEC 60093
Surface resistivity
ROA	1.E + 15	ohms	IEC 60093
Dielectric strength
0.8 mm in oil	46	kV/mm	IEC 60243-1
1.6 mm in oil	31	kV/mm	IEC 60243-1
Relative permittivity
1 MHz	2.9		IEC 60250
Dissipation factor
50-60 Hz	0.002		IEC 60250
Dissipation factor
1 MHz	0.007		IEC 60250
Relative permittivity
50-60 Hz	2.9		IEC 60250

FLAME CHARACTERISTICS	Nominal value	Unit	Test method
94V-1 flame level	0.059	mm	UL 94
94V-0 flame level	0.078	mm	UL 94
Glowing wire flammability index
960 ℃, passed through	0.039	mm	IEC 60695-2-12
Igniting temperature of the hot wire
3 mm	825	℃	IEC 60695-2-13
2 mm	825	℃	IEC 60695-2-13
1 mm	825	℃	IEC 60695-2-13
Extreme oxygen index
LOI	31	%	ISO 4589

Process Conditions
injection molding	Nominal value	Unit	Test method
Drying temperature	180 – 190	°C
Drying time	2 – 4	hrs
Maximum water content	0.02	%
Melt temperature	480 – 570	°C
Nozzle temperature	480 – 570	°C
Front Section Zone 3 Temperature	480 – 570	°C
Temperature in Zone 2 of the middle section	460 – 550	°C
Temperature in Zone 1 of the rear section	450 – 540	°C
Hopper temperature	140 – 180	°C
Mold temperature	140 – 190	°C
Depth of exhaust groove	0.0012 – 0.003	mm

Notes
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.