| Highest impact extrusion ABS for sheet and blow molding applications. FDA food contact compliant.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | ABS |
| Material Status | Commercial: Active |
| Features | High impact resistance,Food contact compliance,HB |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| MECHANICAL | Nominal value | Unit | Test method |
| Tensile modulus | 1680 | MPa | ASTM D638 |
| tensile strength | ASTM D638 | ||
| yield | 35.9 | MPa | |
| fracture | 29.0 | MPa | |
| Tensile strain | ASTM D638 | ||
| yield | 3.5 | % | |
| fracture | 110 | % | |
| Bending modulus | |||
| 50 mm span | 1900 | MPa | ASTM D790 |
| bending strength | |||
| Yield, 50 mm span | 57.9 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | ASTM D256 | ||
| -30℃ | 320 | J/m | |
| 23℃ | 460 | J/m | |
| Dart impact equipped with measuring instruments | |||
| 23℃，Total Energy | 39.5 | J | ASTM D3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 0.45 MPa, unannealed, 3.2 mm | 91.7 | ℃ | |
| 1.8 MPa, unannealed, 3.2 mm | 77.8 | ℃ | |
| Vicat Softening Temp | 106 | ℃ | ASTM D1525 6 |
| Linear coefficient of thermal expansion | ASTM E831 | ||
| MD：-40~40℃ | 1.0E-4 | 1/℃ | |
| TD：-40~40℃ | 1.2E-4 | 1/℃ | |
| Relative temperature index | 60.0 | ℃ | UL 746 |
| Electrical performance | 60.0 | ℃ | UL 746 |
| Impact mechanical performance | 60.0 | ℃ | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.52 mm | HB | UL 94 |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Density | 1.03 | g/cm³ | ASTM D792 |
| Melt Volume Rate | |||
| 220℃，10 kg | 4.00 | cm³/10min | ISO 1133 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.70 to 0.90 | % | Internal Method |
| Apparent viscosity of melt | |||
| 240℃，100 sec^-1 | 1520 | Pa·s | ASTM D3835 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Drying temperature | 87.8 to 93.3 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Recommended maximum moisture content | 1.0E-3 | % | |
| Barrel 1 zone temperature | 193 to 210 | °C | |
| Barrel 2 zone temperature | 199 to 221 | °C | |
| Barrel 3 zone temperature | 204 to 232 | °C | |
| Barrel 4 zone temperature | 210 to 235 | °C | |
| Connector temperature | 199 to 227 | °C | |
| Melt temperature | 210 to 241 | °C | |
| Nozzle temperature | 210 to 241 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.20 in/min |
| 3. Type I, 0.20 in/min |
| 4. 0.051 in/min |
| 5. Rate B (120°C/h), Loading 2 (50 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |