| About |
|---|
| PC+ABS Blend with 10% Glass Reinforce. High flow, High heat resistance., Excellent balance strength/rigidity. Good impact/appearance.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PC+ABS |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Excellent Processability,Good surface appearance,Low contractility,High Heat Resistance |
| Availabilitys | Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.22 | g/cm³ | ISO 1183 |
| Melt Volume Rate | |||
| 260℃，5 kg | 33.0 | cm³/10min | ISO 1133 |
| Shrinkage rate | |||
| MD | 0.30 to 0.50 | % | Internal Method |
| Water absorption rate | |||
| Saturation, 23 ℃ | 0.60 | % | |
| Equilibrium, 23 ℃, 50% RH | 0.20 | % | |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 8.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | |||
| 23℃ | 20 | kJ/m² | ISO 179/1eU |
| Impact strength of cantilever beam notch | |||
| 23℃ | 8.0 | kJ/m² | ISO 180-1A |
| Notched impact strength of cantilever beam | |||
| 23℃ | 20 | kJ/m² | ISO 180/1U |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed, 100 mm span | 133 | ℃ | ISO 75-2/Be |
| 1.8 MPa, unannealed, 100 mm span | 123 | ℃ | ISO 75-2/Ae |
| Vicat Softening Temp | |||
| B50 | 134 | ℃ | ISO 306 |
| B120 | 136 | ℃ | ISO 306/B120 |
| Ball pressure test | |||
| 73~77℃ | 通过 | ||
| 123~127℃ | 通过 | ||
| Linear coefficient of thermal expansion | |||
| MD：-40~40℃ | 4.0E-5 | 1/℃ | |
| TD：-40℃ | 8.0E-5 | 1/℃ | |
| Thermal conductivity coefficient | 0.20 | W/m/K | ISO 8302 |
| Relative temperature index | 60.0 | ℃ | UL 746 |
| Electrical performance | 60.0 | ℃ | UL 746 |
| Impact mechanical performance | 60.0 | ℃ | UL 746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 121 | ISO 2039-2 | |
| Ball hardness | |||
| H358/30 | 116 | MPa | ISO 2039-1 |
| Tensile modulus | 4700 | MPa | ISO 527-1-2 |
| tensile strength | |||
| yield | 90.0 | MPa | |
| fracture | 90.0 | MPa | |
| Tensile strain | |||
| yield | 3.2 | % | |
| fracture | 3.2 | % | |
| Bending modulus | 4250 | MPa | ISO 178 |
| bending strength | |||
| — | 125 | MPa | |
| — | 135 | MPa |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 100 to 110 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Processing (melt) temperature | 240 to 280 | °C | |
| Mold temperature | 50 to 80 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Tensile Bar |
| 3. 0.079 in/min |
| 4. at Break |
| 5. at Yield |
| 6. 80*10*3 sp=62mm |
| 7. 80*10*3 mm |
| 8. 120*10*4 mm |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |