| About |
|---|
| CYCOLOY C6600 Polycarbonate/Acrylonitrile Butadiene Styrene (PC/ABS) resin is a standard grade that can be injection molded. This non-chlorinated, non-brominated flame retardant PC/ABS has a UL V0 & 5VB flame rating. CYCOLOY C6600 resin is an excellent candidate for a wide variety of applications including business equipment, monitors, and enclosures.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PC+ABS |
| Material Status | Commercial: Active |
| Features | High impact resistance,Hydrolysis stability,Good liquidity,Halogen free,Flame Characteristics,V-2,V-0,5VB |
| Availabilitys | North America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.19 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 260℃，2.16kg | 22 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.40 to 0.60 | % | Internal Method |
| Water absorption rate | |||
| 24hr | 0.11 | % | ASTM D570 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 3000 | MPa | ASTM D638 |
| tensile strength | |||
| fracture | 49.0 | MPa | ASTM D638 |
| yield | 63.0 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 80 | % | ASTM D638 |
| yield | 4.0 | % | ASTM D638 |
| Bending modulus | |||
| 50 mm span | 2620 | MPa | ASTM D790 |
| bending strength | |||
| Yield, 50 mm span | 94.0 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 550 | J/m | ASTM D256 |
| Dart impact equipped with measuring instruments | ASTM D3763 | ||
| -30°C，总能量 | 51.0 | J | ASTM D3763 |
| 23 ℃, total energy | 51.0 | J | ASTM D3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 0.45 MPa, unannealed, 6.4 mm | 98.0 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 3.2 mm | 83.0 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 6.4 mm | 90.0 | ℃ | ASTM D648 |
| Vicat Softening Temp | 99.0 | ℃ | ASTM D1525 5 |
| Relative temperature index | |||
| static state | 80.0 | ℃ | UL 746 |
| Electrical performance | 80.0 | ℃ | UL 746 |
| Impact mechanical performance | 70.0 | ℃ | UL 746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric strength | |||
| 3.2 mm in oil | 17 | kV/mm | IEC 60243-1 |
| Relative permittivity | IEC 60250 | ||
| 50 Hz | 2.70 | IEC 60250 | |
| 60 Hz | 2.70 | IEC 60250 | |
| 1 MHz | 2.70 | IEC 60250 | |
| Dissipation factor | IEC 60250 | ||
| 50 Hz | 4.0E-3 | IEC 60250 | |
| 60 Hz | 4.0E-3 | IEC 60250 | |
| 1 MHz | 6.0E-3 | IEC 60250 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 0.75 mm | V-2 | UL 94 | |
| 1.50 mm | V-0 | UL 94 | |
| 2.00 mm | 5VB | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 82 – 88 | °C | |
| Drying time | 3.0 – 4.0 | hr | |
| Drying time, maximum | 8.0 | hr | |
| Recommended maximum moisture content | 0.040 | % | |
| Recommended injection volume | 30 – 80 | % | |
| Barrel rear temperature | 221 – 254 | °C | |
| Barrel middle temperature | 221 – 277 | °C | |
| Barrel front temperature | 243 – 277 | °C | |
| Nozzle temperature | 243 – 277 | °C | |
| Processing (melt) temperature | 243 – 277 | °C | |
| Mold temperature | 60 – 82 | °C | |
| Back pressure | 0.345 – 0.689 | MPa | |
| Screw speed | 40 – 70 | rpm | |
| Vent depth | 0.038 – 0.076 | mm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 in/min |
| 3. Type I, 2.0 in/min |
| 4. 0.051 in/min |
| 5. Rate A (50°C/h), Loading 2 (50 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |