| CYCOLOY CM6210 Polycarbonate/Acrylonitrile Butadiene Styrene (PC/ABS) resin is a mineral filled, low warpage grade that can be injection molded or extruded into sheet for secondary thermoforming operations. This non-chlorinated, non-brominated flame retardant PC/ABS has a UL V0 flame rating. CYCOLOY CM6210 resin is an excellent candidate for a wide variety of applications including enclosures.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PC+ABS |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Halogen free,Flame Characteristics |
| Availabilitys | North America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | |||
| — | 1.28 | g/cm³ | ASTM D792 |
| — | 1.27 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 260℃，5.0kg | 12 | g/10min | ASTM D1238 |
| Melt Volume Rate | |||
| 260℃，5 kg | 9.00 | cm³/10min | ISO 1133 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.40 to 0.60 | % | Internal Method |
| Water absorption rate | |||
| Saturation, 23 ℃ | 0.30 | % | |
| Equilibrium, 23 ℃, 50% RH | 0.10 | % | |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -30℃ | 10 | kJ/m² | |
| 23℃ | 45 | kJ/m² | |
| Impact strength of cantilever beam notch | |||
| -30℃ | 90 | J/m | ASTM D256 |
| 23℃ | 500 | J/m | ASTM D256 |
| -30℃ | 10 | kJ/m² | ISO 180-1A |
| 23℃ | 45 | kJ/m² | ISO 180-1A |
| Dart impact equipped with measuring instruments | |||
| 23℃，Total Energy | 45.0 | J | ASTM D3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed, 100 mm span | 99.0 | ℃ | ISO 75-2/Be |
| 1.8 MPa, unannealed, 3.2 mm | 90.0 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 100 mm span | 89.0 | ℃ | ISO 75-2/Ae |
| Vicat Softening Temp | |||
| — | 106 | ℃ | ASTM D1525 11 |
| B50 | 112 | ℃ | ISO 306 |
| B120 | 114 | ℃ | ISO 306/B120 |
| Ball pressure test | |||
| 73~77℃ | 通过 | ||
| 95℃ | 通过 | ||
| Linear coefficient of thermal expansion | |||
| MD：-40~40℃ | 5.7E-5 | 1/℃ | ASTM E831 |
| MD：-40~40℃ | 5.2E-5 | 1/℃ | ISO 11359-2 |
| MD：23~60℃ | 5.2E-5 | 1/℃ | ISO 11359-2 |
| TD：-40~40℃ | 7.0E-5 | 1/℃ | ASTM E831 |
| TD：-40℃ | 6.0E-5 | 1/℃ | ISO 11359-2 |
| TD：23~60℃ | 6.0E-5 | 1/℃ | ISO 11359-2 |
| Thermal conductivity coefficient | 0.30 | W/m/K | ISO 8302 |
| Relative temperature index | 60.0 | ℃ | UL 746 |
| Electrical performance | 60.0 | ℃ | UL 746 |
| Impact mechanical performance | 60.0 | ℃ | UL 746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Dielectric strength | |||
| 0.8 mm in oil | 38 | kV/mm | |
| 1.6 mm in oil | 26 | kV/mm | |
| 3.2 mm in oil | 17 | kV/mm | |
| Relative permittivity | |||
| 50 Hz | 2.90 | ||
| 60 Hz | 2.90 | ||
| 1 MHz | 2.80 | ||
| Dissipation factor | |||
| 50 Hz | 3.0E-3 | ||
| 60 Hz | 3.0E-3 | ||
| 1 MHz | 4.0E-3 | ||
| Compared to the leakage tracing index | 250 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.50 mm | V-0 | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 98 | ISO 2039-2 | |
| Tensile modulus | |||
| — | 3570 | MPa | ASTM D638 |
| — | 3660 | MPa | ISO 527-1-2 |
| tensile strength | |||
| yield | 64.0 | MPa | ASTM D638 |
| yield | 59.0 | MPa | ISO 527-2/5 |
| yield | 63.0 | MPa | ISO 527-2/50 |
| fracture | 50.0 | MPa | ASTM D638 |
| fracture | 65.0 | MPa | ISO 527-2/5 |
| fracture | 50.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| yield | 4.9 | % | ASTM D638 |
| yield | 3.6 | % | ISO 527-2/5 |
| yield | 3.5 | % | ISO 527-2/50 |
| fracture | 80 | % | ASTM D638 |
| fracture | 100 | % | ISO 527-2/5 |
| fracture | 97 | % | ISO 527-2/50 |
| Bending modulus | |||
| 50 mm span | 3500 | MPa | ASTM D790 |
| — | 3560 | MPa | ISO 178 |
| bending strength | |||
| — | 106 | MPa | ISO 178 |
| Yield, 50 mm span | 110 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| Squeeze description | Nominal value | Unit | Test method |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.20 in/min |
| 3. Type I, 0.20 in/min |
| 4. 0.051 in/min |
| 5. 0.079 in/min |
| 6. at Yield |
| 7. 80*10*3 sp=62mm |
| 8. 80*10*3 mm |
| 9. 120*10*4 mm |
| 10. Rate A (50°C/h), Loading 2 (50 N) |
| 11. Approximate Maximum |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |