| About |
|---|
| CYCOLOY CY6110 Polycarbonate/Acrylonitrile Butadiene Styrene (PC/ABS) resin is a hydrolytically stable, impact modified grade that can be injection molded. This non-chlorinated, non-brominated flame retardant PC/ABS has a UL V0 & 5VB flame rating. CYCOLOY CY6110 resin is an excellent candidate for a wide variety of large size of applications including appliances, lighting, electrical and enclosures.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PC+ABS |
| Material Status | Commercial: Active |
| Features | High impact resistance,Good liquidity,Flame Characteristics,Hydrolysis stability,Halogen free |
| Availabilitys | Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.18 | g/cm³ | ISO 1183 |
| Melt Volume Rate | |||
| 260℃，2.16 kg | 23.0 | cm³/10min | ISO 1133 |
| Molding shrinkage | |||
| MD：3.2 mm | 0.40 to 0.60 | % | Internal Method |
| Water Absorption | |||
| Saturated, 23 ℃ | 0.60 | % | ISO 62 |
| Balanced Equilibrium, 23 ℃, 50% RH | 0.20 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile Modulus | |||
| — | 2760 | MPa | ASTM D638 |
| — | 2750 | MPa | ISO 527-1-2 |
| Tensile Strength | |||
| Yield yld | 63.0 | MPa | ASTM D638 |
| Yield yld | 63.0 | MPa | ISO 527-2/50 |
| Broken BRK | 47.0 | MPa | ASTM D638 |
| Broken BRK | 46.0 | MPa | ISO 527-2/50 |
| Tensile Strain | |||
| Yield yld | 4.1 | % | ASTM D638 |
| Yield yld | 4.0 | % | ISO 527-2/50 |
| Broken BRK | 65 | % | ASTM D638 |
| Broken BRK | 35 | % | ISO 527-2/50 |
| Flexural Modulus | 2440 | MPa | ISO 178 |
| Flexural Strength | 94.0 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -30℃ | 10 | kJ/m² | ISO 179/1eA |
| 23℃ | 33 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | |||
| -30℃ | 无断裂 | ISO 179/1eU | |
| 23℃ | 无断裂 | ISO 179/1eU | |
| Izod Notched Impact strength | |||
| -30℃ | 100 | J/m | ASTM D256 |
| 23℃ | 480 | J/m | ASTM D256 |
| -30℃ | 12 | kJ/m² | ISO 180-1A |
| 23℃ | 25 | kJ/m² | ISO 180-1A |
| Izod Unnotched Impact strength of cantilever beam | |||
| -30℃ | 无断裂 | ISO 180/1U | |
| 23℃ | 无断裂 | ISO 180/1U |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature HDT | |||
| 0.45 MPa, unannealed, 4.0 mm, 64 mm span | 98.0 | ℃ | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 4.0 mm, 64 mm span | 88.0 | ℃ | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| B50 | 104 | ℃ | ISO 306 |
| B120 | 106 | ℃ | ISO 306/B120 |
| Ball Pressure Test | |||
| 73~77℃ | 通过 | IEC 60695-10-2 | |
| Coeff. of linear thermal expansion | |||
| MD：-40~40℃ | 8.0 | 1/℃ | ISO 11359-2 |
| TD：-40℃ | 8.0 | 1/℃ | ISO 11359-2 |
| Relative Temperature Index (RTI) | 85.0 | ℃ | UL 746 |
| Electrical performance Elec | 85.0 | ℃ | UL 746 |
| Impact mechanical performance Imp | 85.0 | ℃ | UL 746 |
| ELECTRICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistance | > 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric Strength | |||
| 0.8 mm, oil in oil | 46 | kV/mm | IEC 60243-1 |
| 1.6 mm, oil in oil | 31 | kV/mm | IEC 60243-1 |
| Relative permittivity | |||
| 50 Hz | 2.90 | IEC 60250 | |
| 60 Hz | 2.90 | IEC 60250 | |
| 1 MHz | 2.90 | IEC 60250 | |
| Dissipation Factor | |||
| 50 Hz | 2.0E-3 | IEC 60250 | |
| 60 Hz | 2.0E-3 | IEC 60250 | |
| 1 MHz | 7.0E-3 | IEC 60250 | |
| Compared Tracking Index | PLC 2 | UL 746 | |
| Hot wire ignition | |||
| HWI | PLC 3 | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame Class Rating | |||
| 1.50 mm | V-0 | UL 94 | |
| 1.50 mm | V-0 | UL 94 | |
| 2.50 mm | 5VB | UL 94 | |
| Glow Wire Flammability Index GWFI | |||
| 0.75 mm | 960 | ℃ | IEC60695 |
| 1.0 mm | 960 | ℃ | IEC60695 |
| Glow Wire Ignitability Temperature (GWIT) | |||
| 0.75 mm | 775 | ℃ | IEC 60695-2-13 |
| 1 mm | 825 | ℃ | IEC 60695-2-13 |
| 1.5 mm | 775 | ℃ | IEC 60695-2-13 |
| 2 mm | 825 | ℃ | IEC 60695-2-13 |
| 3 mm | 825 | ℃ | IEC 60695-2-13 |
| 3 mm | 775 | ℃ | IEC 60695-2-13 |
| Oxygen Index | 31 | % | ISO 4589-2 |
| Process Conditions | |||
|---|---|---|---|
| Injection Molding | Nominal value | Unit | Test method |
| Drying Temperature | 80 to 90 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Maximum Moisture Content | 0.020 | % | |
| Hopper Temperature | 60 to 80 | °C | |
| Rear Temperature Zone 1 | 230 to 280 | °C | |
| Middle Temperature Zone 2 | 240 to 290 | °C | |
| Front Temperature Zone 3 | 250 to 300 | °C | |
| Nozzle temperature | 250 to 300 | °C | |
| Melt Temperature | 250 to 300 | °C | |
| Mold Temperature | 60 to 85 | °C | |
| Exhaust hole depth | 0.030 to 0.075 | mm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.20 in/min |
| 3. Type I, 2.0 in/min |
| 4. 0.079 in/min |
| 5. at Yield |
| 6. 80*10*4 sp=62mm |
| 7. 80*10*4 mm |
| 8. by VDE |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |