| CYCOLOY C7230P resin is a mineral filled, flame retardant PC/ABS. Good stiffness combined with balanced flow and impact performance, makes it a good candidate for various applications.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PC+ABS |
| Material Status | Commercial: Active |
| Features | Good Rigidity,High impact resistance,Good liquidity,Flame Characteristics |
| Availabilitys | Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.30 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 260℃，2.16kg | 13 | g/10min | ASTM D1238 |
| Melt Volume Rate | |||
| 260℃，2.16 kg | 9.00 | cm³/10min | ISO 1133 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.25 to 0.35 | % | Internal Method |
| Water absorption rate | |||
| Saturation, 23 ℃ | 0.090 | % | |
| Equilibrium, 23 ℃, 50% RH | 0.040 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| — | 5190 | MPa | ASTM D638 |
| — | 5580 | MPa | ISO 527-1-2 |
| tensile strength | |||
| yield | 55.0 | MPa | ASTM D638 |
| yield | 55.0 | MPa | ISO 527-2/50 |
| fracture | 43.0 | MPa | ASTM D638 |
| fracture | 35.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| yield | 4.0 | % | ASTM D638 |
| yield | 3.8 | % | ISO 527-2/50 |
| fracture | 30 | % | ISO 527-2/50 |
| Bending modulus | |||
| 50 mm span | 4530 | MPa | ASTM D790 |
| — | 4580 | MPa | ISO 178 |
| bending strength | |||
| — | 99.0 | MPa | ISO 178 |
| Yield, 50 mm span | 95.0 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 5.0 | kJ/m² | ISO 179/1eA |
| Impact strength of cantilever beam notch | |||
| -30℃ | 48 | J/m | ASTM D256 |
| 23℃ | 65 | J/m | ASTM D256 |
| -30℃ | 5.0 | kJ/m² | ISO 180-1A |
| 23℃ | 5.0 | kJ/m² | ISO 180-1A |
| Dart impact equipped with measuring instruments | |||
| 23℃，Total Energy | 0.00 | J | ASTM D3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 3.2 mm | 88.0 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 4.0 mm, 64 mm span | 89.0 | ℃ | ISO 75-2/Af |
| Vicat Softening Temp | |||
| — | 108 | ℃ | ASTM D1525 10 |
| B50 | 107 | ℃ | ISO 306 |
| B120 | 110 | ℃ | ISO 306/B120 |
| Linear coefficient of thermal expansion | |||
| MD：-40~40℃ | 4.2E-5 | 1/℃ | ASTM E831 |
| TD：-40~40℃ | 4.9E-5 | 1/℃ | ASTM E831 |
| TD：-40℃ | 5.9E-5 | 1/℃ | ISO 11359-2 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.20 mm | V-0 | ||
| 2.00 mm | 5VB |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 to 90 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.040 | % | |
| Recommended injection volume | 30 to 80 | % | |
| Barrel rear temperature | 220 to 255 | °C | |
| Barrel middle temperature | 220 to 265 | °C | |
| Barrel front temperature | 245 to 275 | °C | |
| Nozzle temperature | 245 to 275 | °C | |
| Processing (melt) temperature | 245 to 275 | °C | |
| Mold temperature | 60 to 80 | °C | |
| Back pressure | 0.300 to 0.700 | MPa | |
| Screw speed | 40 to 70 | rpm | |
| Vent depth | 0.038 to 0.076 | mm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.20 in/min |
| 3. Type I, 2.0 in/min |
| 4. 0.051 in/min |
| 5. 0.079 in/min |
| 6. at Yield |
| 7. 80*10*4 sp=62mm |
| 8. 80*10*4 mm |
| 9. Rate A (50°C/h), Loading 2 (50 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |