| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PC+ABS |
| Material Status | Commercial: Active |
| Features | Good liquidity |
| Availabilitys | North America |
| Technical Data | |||
|---|---|---|---|
| MECHANICAL | Nominal value | Unit | Test method |
| Rockwell hardness | |||
| R-level | 121 | MPa | ISO 2039-2 |
| Ball hardness | |||
| H358/30 | 99 | ISO 2039-1 | |
| tensile strength | |||
| Yield, 50 mm/min | 55 | MPa | ISO 527 |
| Fracture, 50 mm/min | 45 | MPa | ISO 527 |
| Tensile strain | |||
| Yield, 50 mm/min | 5 | % | ISO 527 |
| Fracture, 50 mm/min | 15 | % | ISO 527 |
| Tensile modulus | |||
| 1 mm/min | 2400 | MPa | ISO 527 |
| bending strength | |||
| Yield, 2 mm/min | 82 | MPa | ISO 178 |
| Bending modulus | |||
| 2 mm/mim | 2400 | MPa | ISO 178 |
| tensile strength | |||
| Yield, 5 mm/min | 55 | MPa | ISO 178 |
| Fracture, 5 mm/min | 45 | MPa | ISO 178 |
| Tensile strain | |||
| Yield, 5 mm/min | 5 | % | ISO 178 |
| Fracture, 5 mm/min | 15 | % | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Total energy of instrument impact | |||
| 23℃ | 42 | J | ASTM D 3763 |
| Impact strength of cantilever beam notch | |||
| 23℃ | 43 | J/m | ASTM D256 |
| 23℃，80*10*4 | 24 | kJ/m² | ISO 180-1A |
| 80*10*4 -30℃ | 12 | kJ/m² | ISO 180-1A |
| Charpy Notched Impact Strength | |||
| 80*10*4 | |||
| 23℃ | 25 | kJ/m² | ISO 179/1eA |
| -30℃ | 13 | kJ/m² | ISO 179/1eA |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 143 | ℃ | ASTM D1525 |
| Thermal conductivity coefficient | 0.2 | W/m/℃ | ISO 8302 |
| Hot deformation temperature | |||
| 0.45 MPa, 100 mm span | 128 | ℃ | ISO 75/Be |
| 1.8 MPa, 100 mm span | 108 | ℃ | ISO 75/Ae |
| Unannealed, 3.2 mm | |||
| 0.45 MPa | 131 | ℃ | ASTM D 648 |
| 1.8MPa | 112 | ℃ | ASTM D 648 |
| Linear expansion coefficient, -40 ℃ to 40 ℃ | |||
| flow | 7.2E-05 | 1/℃ | ASTM E 831 |
| transverse | 7.2E-05 | 1/℃ | ASTM E 831 |
| Ball pressure test | |||
| 125℃±2℃ | PASSES | IEC 60695-10-2 | |
| Linear expansion coefficient, 23 ℃ to 60 ℃ | |||
| flow | 8.E-05 | ISO 11359-2 | |
| transverse | 8.E-05 | ISO 11359-2 | |
| Vicat Softening Temp | |||
| B50 | 128 | ℃ | ISO 306 |
| B120 | 130 | ℃ | ISO 306 |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Density | 1.18 | ASTM D792 | |
| Shrinkage rate | |||
| MD：3.2 mm | 0.4 – 0.6 | % | Internal Method |
| Melt Flow Rate | |||
| 260℃，5.0kg | 22 | g/10min | ASTM D1238 |
| Density | 1.18 | g/cm³ | ISO 1183 |
| Melt Volume Rate | |||
| 260℃，5 kg | 22 | cm³/10min | ISO 1133 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Dielectric strength | |||
| In oil | |||
| 0.8 mm | 35 | kV/mm | IEC 60243-1 |
| 1.6mm | 25 | kV/mm | IEC 60243-1 |
| 3.2 mm | 17 | kV/mm | IEC 60243-1 |
| Volume resistivity | > 1.E+15 | ohms·cm | IEC 60093 |
| Surface resistivity | >1.0E+15 | IEC 60093 | |
| Relative permittivity | |||
| 50-60 Hz | 2.8 | IEC 60250 | |
| 1 MHz | 2.7 | IEC 60250 | |
| Dissipation factor | |||
| 50-60 Hz | 0.003 | IEC 60250 | |
| 1 MHz | 0.005 | IEC 60250 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |