CYCOLOY™ FXC813SK resin

About
CYCOLOY™ FXC813SK 是一种多用途的PC + ABS注塑成型树脂，提供了良好的工程平衡性能，适用于需要减少流线外观的闪烁的色彩效果的应用。

Product Description
Supplier	SABIC
Generic	PC+ABS
Material Status	Commercial: Active
Features	Rigid-tough balance
Availabilitys	Africa & Middle East ,Asia Pacific,Europe

Technical Data
MECHANICAL	Nominal value	Unit	Test method
Taber wear and tear
CS-17，1kg	63	mg/1000cy	Internal Method
Rockwell hardness
R-level	121	MPa	ISO 2039-2
Ball hardness
H358/30	99		ISO 2039-1
tensile strength
Yield, 50 mm/min	55	MPa	ISO 527
Fracture, 50 mm/min	45	MPa	ISO 527
Tensile strain
Yield, 50 mm/min	5	%	ISO 527
Fracture, 50 mm/min	15	%	ISO 527
Tensile modulus
1 mm/min	2400	MPa	ISO 527
bending strength
Yield, 2 mm/min	82	MPa	ISO 178
Bending modulus
2 mm/mim	2400	MPa	ISO 178
tensile strength
Yield, 5 mm/min	55	MPa	ISO 178
Fracture, 5 mm/min	45	MPa	ISO 178
Tensile strain
Yield, 5 mm/min	5	%	ISO 178
Fracture, 5 mm/min	15	%	ISO 178

IMPACT	Nominal value	Unit	Test method
Impact strength of cantilever beam notch
23℃，80103	25	kJ/m²	ISO 180-1A
-30℃，80103	12	kJ/m²	ISO 180-1A
Charpy Notched Impact Strength
80103
23℃	25	kJ/m²	ISO 179/1eA
-30℃	12	kJ/m²	ISO 179/1eA

THERMAL	Nominal value	Unit	Test method
Thermal conductivity coefficient	0.2	W/m/℃	ISO 8302
Linear expansion coefficient, -40 ℃ to 40 ℃
flow	8.E-05	1/℃	ISO 11359-2
transverse	8.E-05	1/℃	ISO 11359-2
Ball pressure test
125℃±2℃	PASSES		IEC 60695-10-2
Vicat Softening Temp
B50	128	℃	ISO 306
B120	130	℃	ISO 306
Hot deformation temperature
0.45 MPa, 100 mm span	128	℃	ISO 75/Be
1.8 MPa, 100 mm span	108	℃	ISO 75/Ae

PHYSICAL	Nominal value	Unit	Test method
Shrinkage rate
MD：3.2 mm	0.5 – 0.7	%	Internal Method
Melt Volume Rate
260℃，5 kg	22	cm³/10min	ISO 1133
Density	1.18	g/cm³	ISO 1183
Water absorption rate
Saturation, 23 ℃	0.6	%	ISO 62
23℃，50% RH	0.2	%	ISO 62

Electrical performance	Nominal value	Unit	Test method
Dielectric strength
In oil
0.8 mm	35	kV/mm	IEC 60243-1
1.6mm	25	kV/mm	IEC 60243-1
3.2 mm	17	kV/mm	IEC 60243-1
Volume resistivity	> 1.E+15	ohms·cm	ASTM D257
Surface resistivity	> 1.0E+15	ohms/sq	ASTM D257
Relative permittivity
50-60 Hz	2.8		IEC 60250
1 MHz	2.7		IEC 60250
Dissipation factor
50-60 Hz	0.003		IEC 60250
1 MHz	0.005		IEC 60250
Compared to the leakage tracing index	600	V	IEC 60112

FLAME CHARACTERISTICS	Nominal value	Unit	Test method
94HB flame rating assessment	1.2	mm	UL 944 by SABIC-IP
94HB flame rating evaluation second reference value	3	mm	UL 944 by SABIC-IP
Glowing wire flammability index
650 ℃, passed through	1	mm	IEC 60695-2-12
Extreme oxygen index
LOI	23	%	ISO 4589

Process Conditions
injection molding	Nominal value	Unit	Test method
Drying temperature	100 – 110	°C
Drying time	2 – 4	hrs
Maximum water content	0.02	%
Melt temperature	260 – 290	°C
Nozzle temperature	240 – 280	°C
Temperature of barrel zone 1	250 – 290	°C
Temperature of barrel zone 2	250 – 290	°C
Barrel Zone 3 Temperature	230 – 260	°C
Hopper temperature	60 – 80	°C
Mold temperature	60 – 90	°C

Notes
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.