| About |
|---|
| CYCOLOY HCX1640 Polycarbonate/Acrylonitrile Butadiene Styrene (PC/ABS) resin is an improved chemical resistance, impact modified, biocompatible grade that can be injection molded. This Healthcare Management of Change grade CYCOLOY HCX1640 resin is an excellent candidate for a wide variety of medical and pharmaceutical devices.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PC+ABS |
| Material Status | Commercial: Active |
| Features | High impact resistance,Ductility,Good liquidity,Biocompatible |
| Availabilitys | Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.15 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Flow Rate | |||
| 260℃，5.0kg | 19 | g/10min | ASTM D1238 |
| Melt Volume Rate | |||
| 260℃，5 kg | 18.0 | cm³/10min | ISO 1133 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.40 to 0.60 | % | Internal Method |
| Water absorption rate | ISO 62 | ||
| Saturation, 23 ℃ | 0.40 | % | |
| Equilibrium, 23 ℃, 50% RH | 0.10 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| — | 2400 | MPa | ASTM D638 |
| — | 2400 | MPa | ISO 527-1-2 |
| tensile strength | |||
| yield | 55.0 | MPa | ASTM D638 |
| yield | 55.0 | MPa | ISO 527-2/50 |
| fracture | 50.0 | MPa | ASTM D638 |
| fracture | 50.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| yield | 5.0 | % | ASTM D638 |
| yield | 5.0 | % | ISO 527-2/50 |
| fracture | > 50 | % | ASTM D638 |
| fracture | > 50 | % | ISO 527-2/50 |
| Bending modulus | |||
| 50 mm span | 2300 | MPa | ASTM D790 |
| — | 2300 | MPa | ISO 178 |
| bending strength | |||
| — | 85.0 | MPa | ISO 178 |
| Yield, 50 mm span | 85.0 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30℃ | 20 20 | kJ/m² | |
| 23℃ | 40 40 | kJ/m² | |
| Charpy Unnotch Impact strength | ISO 179/1eU | ||
| -30℃ | 无断裂 无断裂 | ||
| 23℃ | 无断裂 无断裂 | ||
| Impact strength of cantilever beam notch | |||
| -30℃ | 300 | J/m | ASTM D256 |
| 23℃ | 550 | J/m | ASTM D256 |
| -30℃ | 20 20 | kJ/m² | ISO 180-1A |
| 23℃ | 40 40 | kJ/m² | ISO 180-1A |
| Notched impact strength of cantilever beam | |||
| 23℃ | 150 | J/m | Internal Method |
| -30℃ | 无断裂 无断裂 | ISO 180/1U | |
| 23℃ | 无断裂 无断裂 | ISO 180/1U | |
| Dart impact equipped with measuring instruments | |||
| 23℃，Total Energy | 65.0 | J | ASTM D3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed, 3.2 mm | 122 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 3.2 mm | 108 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 64 mm span | 108 | ℃ | ISO 75-2/Af |
| Vicat Softening Temp | |||
| B50 | 130 | ℃ | ASTM D1525, ISO 306/B50 11 18 |
| B120 | 132 | ℃ | ISO 306/B120 |
| Linear coefficient of thermal expansion | ASTM E831, ISO 11359-2 | ||
| MD：-40~40℃ | 7.0E-5 | 1/℃ | |
| TD：-40~40℃ | 7.0E-5 | 1/℃ |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 100 to 110 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Hopper temperature | 60.0 to 80.0 | °C | |
| Barrel rear temperature | 230 to 260 | °C | |
| Barrel middle temperature | 250 to 290 | °C | |
| Barrel front temperature | 250 to 290 | °C | |
| Nozzle temperature | 240 to 280 | °C | |
| Processing (melt) temperature | 260 to 290 | °C | |
| Mold temperature | 60.0 to 90.0 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.20 in/min |
| 3. Type I, 2.0 in/min |
| 4. 0.051 in/min |
| 5. 0.079 in/min |
| 6. at Yield |
| 7. 80*10*4 sp=62mm |
| 8. Double-gated |
| 9. 80*10*4 mm |
| 10. Rate A (50°C/h), Loading 2 (50 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |