| About |
|---|
| PC/ABS low gloss.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PC+ABS |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,High impact resistance,High Heat Resistance,Low Gloss,HB |
| Availabilitys | North America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.13 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 260℃，5.0kg | 17 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| TD：3.2 mm | 0.50 to 0.70 | % | Internal Method |
| MD：3.2 mm | 0.50 to 0.70 | % | Internal Method |
| Water absorption rate | |||
| Equilibrium, 23 ℃ | 0.40 | % | ASTM D570 |
| 24hr | 0.10 | % | ASTM D570 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | ASTM D256 | ||
| -30℃ | 320 | J/m | ASTM D256 |
| 23℃ | 530 | J/m | ASTM D256 |
| Dart impact equipped with measuring instruments | ASTM D3763 | ||
| -30℃，Total Energy | 33.9 | J | ASTM D3763 |
| 23℃，Total Energy | 40.7 | J | ASTM D3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 0.45 MPa, unannealed, 3.2 mm | 124 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed, 6.4 mm | 129 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 3.2 mm | 107 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 6.4 mm | 110 | ℃ | ASTM D648 |
| Vicat Softening Temp | 129 | ℃ | ASTM D1525 |
| Linear coefficient of thermal expansion | |||
| TD：-20：150℃ | 7.2E-5 | 1/℃ | ASTM E831 |
| MD：-20~150℃ | 7.2E-5 | 1/℃ | ASTM E831 |
| Thermal conductivity coefficient | 0.20 | W/m/K | ASTM C177 |
| Relative temperature index | |||
| Electrical performance | 60.0 | ℃ | UL 746 |
| Strength mechanical performance | 60.0 | ℃ | UL 746 |
| Impact mechanical performance | 60.0 | ℃ | UL 746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Arc resistance | PLC 6 | ASTM D495 | |
| Compared to the leakage tracing index | PLC 2 | UL 746 | |
| High Arc Burning Index (HAI) | PLC 0 | UL 746 | |
| Hot wire ignition | |||
| HWI | PLC 2 | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.50 mm | HB | UL 94 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 60 °, no texture | 30 | ASTM D523 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| yield | 54.5 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 75 | % | ASTM D638 |
| Bending modulus | |||
| 50 mm span | 2310 | MPa | ASTM D790 |
| bending strength | |||
| Yield, 50 mm span | 84.8 | MPa | ASTM D790 |
| Rockwell hardness | |||
| R-level | 118 | ASTM D785 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 104 to 110 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Drying time, maximum | 8.0 | hr | |
| Recommended maximum moisture content | 0.040 | % | |
| Recommended injection volume | 30 to 80 | % | |
| Barrel rear temperature | 249 to 288 | °C | |
| Barrel middle temperature | 254 to 293 | °C | |
| Barrel front temperature | 260 to 302 | °C | |
| Nozzle temperature | 274 to 302 | °C | |
| Processing (melt) temperature | 274 to 302 | °C | |
| Mold temperature | 60 to 88 | °C | |
| Back pressure | 0.345 to 0.689 | MPa | |
| Screw speed | 40 to 70 | rpm | |
| Vent depth | 0.038 to 0.076 | mm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Type I, 2.0 in/min |
| 3. 0.051 in/min |
| 4. Rate B (120°C/h), Loading 2 (50 N) |
| 5. Tungsten Electrode |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |