| About |
|---|
| High heat PC/ABS blend offering good flow and excellent impact. |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PC+ABS |
| Material Status | Commercial: Active |
| Features | High impact resistance,Good liquidity,High Heat Resistance |
| Availabilitys | North America,Latin America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Melt Flow Rate | |||
| 260℃，5.0kg | 17 | g/10min | ASTM D1238 |
| Melt Volume Rate | |||
| 260℃，5 kg | 18.0 | cm³/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| — | 2250 | MPa | ASTM D638 |
| — | 2180 | MPa | ISO 527-1-2 |
| Tensile strength | |||
| yield | 53.0 | MPa | ASTM D638 |
| yield | 52.0 | MPa | ISO 527-2/50 |
| fracture | 45.0 | MPa | ASTM D638 |
| fracture | 46.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| yield | 4.8 | % | ASTM D638 |
| yield | 4.7 | % | ISO 527-2/50 |
| fracture | 93 | % | ASTM D638 |
| fracture | 100 | % | ISO 527-2/50 |
| Bending modulus | |||
| 50 mm span | 2310 | MPa | ASTM D790 |
| — | 2140 | MPa | ISO 178 |
| Bending stress | |||
| — | 81.0 | MPa | ISO 178 |
| Yield, 50.0 mm span | 83.0 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 56 | kJ/m² | ISO 179/1eA |
| Impact strength of cantilever beam notch | |||
| -30℃ | 430 | J/m | ASTM D256 |
| 0℃ | 510 | J/m | ASTM D256 |
| 23℃ | 580 | J/m | ASTM D256 |
| -30℃ | 37 | kJ/m² | ISO 180-1A |
| 0℃ | 40 | kJ/m² | ISO 180-1A |
| 23℃ | 45 | kJ/m² | ISO 180-1A |
| Dart impact equipped with measuring instruments | |||
| 23°C，Energy at Peak | 51.0 | J | |
| 23°C，Total Energy | 59.0 | J |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed, 3.2 mm | 128 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed, 4.0 mm, 64 mm span | 128 | ℃ | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 3.2 mm | 106 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 4.0 mm, 64 mm span | 103 | ℃ | ISO 75-2/Af |
| Vicat Softening Temp | 121 | ℃ | ISO 306/B50 |
| Process Conditions | |||
|---|---|---|---|
| Injection | Nominal value | Unit | Test method |
| drying temperature | 100 to 110 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Hopper temperature | 60 to 80 | °C | |
| Temperature at the rear of the barrel | 230 to 260 | °C | |
| Temperature in the middle of the barrel | 250 to 290 | °C | |
| Front temperature of material barrel | 250 to 290 | °C | |
| Nozzle temperature | 240 to 280 | °C | |
| Processing (melt) temperature | 260 to 290 | °C | |
| Mold temperature | 60 to 90 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |