High heat PC/ABS blend offering high modulus / low CTE and good practical impact&& |
Product Description | |
---|---|
Supplier | SABIC |
Generic | PC+ABS |
Material Status | Commercial: Active |
Features | High impact resistance,High Heat Resistance |
Availabilitys | North America |
Technical Data | |||
---|---|---|---|
PHYSICAL | Nominal value | Unit | Test method |
Density | 1.30 | g/cm³ | ASTM D792 |
Density | 1.30 | g/cm³ | ISO 1183 |
Melt Flow Rate | |||
260℃,5.0kg | 12 | g/10min | ASTM D1238 |
Melt Volume Rate | |||
260℃,5 kg | 9.00 | cm³/10min | ISO 1133 |
Shrinkage rate | |||
MD:3.2 mm | 0.30 to 0.50 | % | Internal Method |
Water absorption rate | |||
Saturation, 23 ℃ | 0.20 | % | ISO 62 |
Equilibrium, 23 ℃, 50% RH | 0.010 | % | ISO 62 |
MECHANICAL | Nominal value | Unit | Test method |
---|---|---|---|
Tensile modulus | 4750 | MPa | ASTM D638 |
Tensile modulus | 4600 | MPa | ISO 527-1-2 |
tensile strength | |||
fracture | 45.0 | MPa | ISO 527-2/5 |
fracture | 35.0 | MPa | ASTM D638 |
yield | 60.0 | MPa | ASTM D638 |
yield | 55.0 | MPa | ISO 527-2/5 |
Tensile strain | |||
fracture | 12 | % | ASTM D638 |
fracture | 10 | % | ISO 527-2/5 |
yield | 4.0 | % | ISO 527-2/5 |
yield | 4.0 | % | ASTM D638 |
Bending modulus | 4400 | MPa | ISO 178 |
50 mm span | 4550 | MPa | ASTM D790 |
bending strength | 100 | MPa | ISO 178 |
bending strength | |||
Yield, 50 mm span | 108 | MPa | ASTM D790 |
IMPACT | Nominal value | Unit | Test method |
---|---|---|---|
Charpy Notched Impact Strength | |||
23℃ | 15 | kJ/m² | ISO 179/1eA |
Charpy Unnotch Impact strength | |||
23℃ | No Break | ISO 179/1eU | |
Impact strength of cantilever beam notch | ASTM D256 | ||
-30℃ | 80 | J/m | ASTM D256 |
23℃ | 100 | J/m | ASTM D256 |
Impact strength of cantilever beam notch | ISO 180/1A | ||
-30℃ | 9.0 | kJ/m² | ISO 180-1A |
23℃ | 12 | kJ/m² | ISO 180-1A |
Notched impact strength of cantilever beam | |||
23℃ | No Break | ISO 180/1U | |
Dart impact equipped with measuring instruments | |||
23℃,Total Energy | 60.0 | J | ASTM D3763 |
THERMAL | Nominal value | Unit | Test method |
---|---|---|---|
Hot deformation temperature | |||
1.8 MPa, unannealed, 64 mm span | 122 | ℃ | ISO 75-2/Af |
1.8 MPa, unannealed, 3.2 mm | 119 | ℃ | ASTM D648 |
Vicat Softening Temp | 138 | ℃ | ASTM D1525 10 |
Vicat Softening Temp | |||
B50 | 139 | ℃ | ISO 306 |
B120 | 140 | ℃ | ISO 306/B120 |
Linear coefficient of thermal expansion | |||
TD:-40~40℃ | 5.6E-5 | 1/℃ | ISO 11359-2 |
TD:-40~40℃ | 5.6E-5 | 1/℃ | ASTM E831 |
MD:-40~40℃ | 4.1E-5 | 1/℃ | ISO 11359-2 |
MD:-40~40℃ | 4.1E-5 | 1/℃ | ASTM E831 |
Process Conditions | |||
---|---|---|---|
injection | Nominal value | Unit | Test method |
Extrusion | Nominal value | Unit | Test method |
Drying temperature | 110 to 120 | °C | |
Drying time | 2.0 to 6.0 | hr | |
Recommended maximum moisture content | 0.020 | % | |
Recommended injection volume | 30 to 80 | % | |
Barrel rear temperature | 260 to 270 | °C | |
Barrel middle temperature | 265 to 290 | °C | |
Barrel front temperature | 270 to 300 | °C | |
Nozzle temperature | 260 to 290 | °C | |
Processing (melt) temperature | 270 to 300 | °C | |
Mold temperature | 60 to 100 | °C | |
Back pressure | 0.300 to 0.700 | MPa | |
Screw speed | 40 to 70 | rpm | |
Vent depth | 0.038 to 0.076 | mm | |
Drying temperature | 120 | °C | |
Drying time | 2.0 to 6.0 | hr | |
Recommended maximum moisture content | 0.020 | % | |
Barrel 1 zone temperature | 195 to 205 | °C | |
Barrel 2 zone temperature | 200 to 220 | °C | |
Barrel 3 zone temperature | 220 to 240 | °C | |
Barrel 4 zone temperature | 230 to 260 | °C | |
Connector temperature | 230 to 260 | °C | |
Melt temperature | 250 to 270 | °C | |
Nozzle temperature | 230 to 245 | °C |
Notes |
---|
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |