| About |
|---|
| PC/ABS, hydrolytically stable, colors.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PC+ABS |
| Material Status | Commercial: Active |
| Features | Good heat aging resistance,High impact resistance,High liquidity,Ductility,Hydrolysis stability |
| Availabilitys | North America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| MECHANICAL | Nominal value | Unit | Test method |
| Tensile modulus | 2300 | MPa | ASTM D638 |
| Tensile modulus | 2200 | MPa | ISO 527-1-2 |
| tensile strength | |||
| fracture | 51.0 | MPa | ISO 527-2/50 |
| fracture | 52.0 | MPa | ASTM D638 |
| yield | 54.0 | MPa | ISO 527-2/50 |
| yield | 55.0 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 120 | % | ISO 527-2/50 |
| fracture | 120 | % | ASTM D638 |
| yield | 4.5 | % | ISO 527-2/50 |
| yield | 4.7 | % | ASTM D638 |
| Bending modulus | 2200 | MPa | ISO 178 |
| 50 mm span | 2300 | MPa | ASTM D790 |
| bending strength | 83.0 | MPa | ISO 178 |
| bending strength | |||
| Yield, 50 mm span | 89.0 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30℃ | 45 | kJ/m² | ISO 179/1eA |
| 23℃ | 70 | kJ/m² | ISO 179/1eA |
| 23℃ | 60 | kJ/m² | ISO 179/1eA |
| Impact strength of cantilever beam notch | ASTM D256 | ||
| -30℃ | 480 | J/m | ASTM D256 |
| 23℃ | 640 | J/m | ASTM D256 |
| Impact strength of cantilever beam notch | ISO 180/1A | ||
| -30℃ | 45 | kJ/m² | ISO 180-1A |
| 23℃ | 55 | kJ/m² | ISO 180-1A |
| 23℃ | 70 | kJ/m² | ISO 180-1A |
| Dart impact equipped with measuring instruments | ASTM D3763 | ||
| -30℃，Total Energy | 70.0 | J | ASTM D3763 |
| 23℃，Total Energy | 56.0 | J | ASTM D3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 64 mm span | 105 | ℃ | ISO 75-2/Af |
| 1.8 MPa, unannealed, 3.2 mm | 107 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed, 64 mm span | 126 | ℃ | ISO 75-2/Bf |
| Vicat Softening Temp | 127 | ℃ | ASTM D1525 12 |
| Vicat Softening Temp | |||
| B50 | 127 | ℃ | ISO 306 |
| B120 | 129 | ℃ | ISO 306/B120 |
| Ball pressure test | |||
| 75℃ | Pass | IEC 60695-10-2 | |
| Linear coefficient of thermal expansion | |||
| TD：-40~40℃ | 7.0E-5 | 1/℃ | ISO 11359-2 |
| TD：-40~40℃ | 7.0E-5 | 1/℃ | ASTM E831 |
| MD：-40~40℃ | 7.0E-5 | 1/℃ | ASTM E831 |
| MD：-40~40℃ | 7.0E-5 | 1/℃ | ISO 11359-2 |
| Thermal conductivity coefficient | 0.20 | W/m/K | ISO 8302 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric strength | IEC 60243-1 | ||
| 0.8 mm in oil | 35 | kV/mm | IEC 60243-1 |
| 1.6 mm in oil | 25 | kV/mm | IEC 60243-1 |
| 3.2 mm in oil | 17 | kV/mm | IEC 60243-1 |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Density | 1.14 | g/cm³ | ASTM D792 |
| Density | 1.14 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 260℃，5.0kg | 22 | g/10min | ASTM D1238 |
| Melt Volume Rate | |||
| 260℃，5 kg | 18.0 | cm³/10min | ISO 1133 |
| Shrinkage rate | |||
| TD：3.2 mm | 0.50 to 0.70 | % | Internal Method |
| MD：3.2 mm | 0.50 to 0.70 | % | Internal Method |
| Water absorption rate | |||
| Saturation, 23 ℃ | 0.40 | % | ISO 62 |
| Equilibrium, 23 ℃, 50% RH | 0.15 | % | ISO 62 |
| Apparent viscosity of melt | |||
| 260℃，1500 sec^-1 | 195 | Pa·s | ISO 11443 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 95 to 105 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Drying time, maximum | 8.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Recommended injection volume | 30 to 80 | % | |
| Hopper temperature | 60 to 80 | °C | |
| Barrel rear temperature | 230 to 260 | °C | |
| Barrel middle temperature | 250 to 290 | °C | |
| Barrel front temperature | 250 to 290 | °C | |
| Nozzle temperature | 240 to 280 | °C | |
| Processing (melt) temperature | 260 to 290 | °C | |
| Mold temperature | 60 to 90 | °C | |
| Back pressure | 0.300 to 0.700 | MPa | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.20 in/min |
| 3. Type I, 2.0 in/min |
| 4. 0.051 in/min |
| 5. 0.079 in/min |
| 6. Yield |
| 7. 80*10*3 sp=62mm |
| 8. 80*10*4 sp=62mm |
| 9. 80*10*3 |
| 10. 80*10*4 |
| 11. 80*10*4 mm |
| 12. Rate B (120°C/h), Loading 2 (50 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |