| About |
|---|
| Characteristics: General use, moisture resistant Laser: Ar/solid-state Post-cure: Not needed&& |
| Product Description | |
|---|---|
| Generic | 环氧树脂 |
| Material Status | Commercial: Active |
| Features | Moisture resistance |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.13 | g/cm³ | |
| viscosity | |||
| 25℃ | 0.34 | Pa·s | |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Notched impact strength of cantilever beam | 25 to 27 | J/m |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 53.0 | ℃ | |
| Glass transition temperature | 82.0 | ℃ | DMA |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Critical Exposure | 33.0 | mJ/cm² | |
| Penetration depth | 191.0 | µm |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 87 | ||
| Tensile modulus | 3300 | MPa | |
| tensile strength | 75.0 | MPa | |
| Tensile strain | |||
| fracture | 6.0 | % | |
| Bending modulus | 3100 | MPa | |
| bending strength | 104 | MPa |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Liquid Resin |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |