| Daelim Po1y® XP6070 is a Metallocene High Density Polyethylene product. It is available in Asia Pacific or Europe. Applications of Daelim Po1y® XP6070 include containers, food contact applications, household applications and industrial applications. Characteristics include: Antioxidant Impact Resistant&& |
| Product Description | |
|---|---|
| Generic | mHDPE |
| Material Status | Commercial: Active |
| Features | High impact resistance,Inoxidizability |
| Availabilitys | Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.961 | g/cm³ | ASTM D1505 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 9.5 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD | 1.9 | % | ASTM D955 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| Yield, molding | 27.5 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, molded | > 600 | % | ASTM D638 |
| Bending modulus | |||
| Compression Molding | 1270 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| -30 ℃, molded | No Break | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 90.0 | ℃ | ASTM D648 |
| Vicat Softening Temp | 129 | ℃ | ASTM D1525 |
| Melting peak temperature | 134 | ℃ | ASTM D3418 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Processing (melt) temperature | 200 to 250 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |