DAI-EL™ G-7211

About
DAI-EL™ G-7211 DAI-EL G-7211 is a cure-incorporated copolymer designed for injection transfer and compression molding applications. G-7211 offers low Mooney viscosity with good compression set resistance.&&DAI-EL™ G-7211 DAI-EL G-7211 is a fluoroelastomer comprising copolymer of vinylidenefluoride and hexafluoropropylene, and contains a curing agent (bisphenol AF) and cure accelerator. This material is of the grade of good mold flow and with a sealing property suitable for injection molding. The roll processability of G-7211 has been improved compared with that of G-7201.&&

About

DAI-EL™ G-7211 DAI-EL G-7211 is a cure-incorporated copolymer designed for injection transfer and compression molding applications. G-7211 offers low Mooney viscosity with good compression set resistance.&&DAI-EL™ G-7211 DAI-EL G-7211 is a fluoroelastomer comprising copolymer of vinylidenefluoride and hexafluoropropylene, and contains a curing agent (bisphenol AF) and cure accelerator. This material is of the grade of good mold flow and with a sealing property suitable for injection molding. The roll processability of G-7211 has been improved compared with that of G-7201.&&

Product Description
Supplier	Daikin Fluorochemicals
Generic	氟橡胶
Material Status	Commercial: Active
Features	Good Dimensional Stability,Good liquidity,Low Viscosity,Copolymer
Availabilitys	North America,Asia Pacific

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.81	g/cm³	ASTM D792
Mooney viscosity
ML 1+10，121℃	22	MU	ASTM D1646

MECHANICAL	Nominal value	Unit	Test method
Shore hardness
Shaw’s A	73		ASTM D2240

elastic body	Nominal value	Unit	Test method
tensile strength
yield	14.1	MPa	ASTM D412
100% strain	4.10	MPa	ASTM D412
Tensile strain
fracture	250	%	ASTM D412
tear strength
25℃	23.4	kN/m	ASTM D624
Compression deformation			ASTM D395
25℃，70 hr	9.0	%	ASTM D395
100℃，70 hr	7.0	%	ASTM D395
175℃，70 hr	8.0	%	ASTM D395
200℃，70 hr	11	%	ASTM D395

Aging performance	Nominal value	Unit	Test method
The rate of change in tensile strength in air
230℃，70 hr	2.0	%	ASTM D573
The rate of change in ultimate elongation in air
230℃，70 hr	-8.0	%	ASTM D573
The rate of change in hardness of a hardness tester in the air
Shore A, 230 ℃, 70 hr	2.0		ASTM D573

THERMAL	Nominal value	Unit	Test method
Embrittlement temperature	-17.0	℃	ASTM D746

Notes
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.