Daicel PP PG6N1 is a Polypropylene material filled with 30% glass fiber. It is available in Asia Pacific. Primary attribute of Daicel PP PG6N1: Flame Rated.&&

Product Description
Supplier	Daicel
Generic	PP not specified
Material Status	Commercial: Active
Features	HB
Availabilitys	Asia Pacific

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.12	g/cm³	ISO 1183
Melt Flow Rate
230℃，2.16kg	4.0	g/10min	ISO 1133
Shrinkage rate
MD	0.40 to 0.70	%	ASTM D955

IMPACT	Nominal value	Unit	Test method
Charpy Notched Impact Strength
23℃	13	kJ/m²	ISO 179/1eA

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
0.45 MPa, unannealed	160	℃	ISO 75-2/B

FLAME CHARACTERISTICS	Nominal value	Unit	Test method
Flame retardant level	HB		UL 94

MECHANICAL	Nominal value	Unit	Test method
Rockwell hardness
R-level	111		ISO 2039-2
tensile strength
yield	85.0	MPa	ISO 527-2
Bending modulus	6000	MPa	ISO 178
bending strength	130	MPa	ISO 178

Process Conditions
injection	Nominal value	Unit	Test method
Drying temperature	80.0 to 120	°C
Drying time	3.0 to 5.0	hr
Barrel rear temperature	140 to 190	°C
Barrel middle temperature	160 to 210	°C
Barrel front temperature	180 to 230	°C
Nozzle temperature	180 to 230	°C
Mold temperature	40.0 to 60.0	°C
Back pressure	5.00 to 20.0	MPa
Screw speed	70 to 90	rpm

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.