| About |
|---|
| Daplen EE109AE is a 20% mineral filled elastomer modified polypropylene compound intended for injection moulding. This material has an excellent balance between impact strength and stiffness, gives a good surface quality and is easy to process.&& |
| Product Description | |
|---|---|
| Supplier | Borealis AG |
| Generic | PP not specified |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Excellent Processability,Good surface appearance,High impact resistance,Sprayable |
| Availabilitys | Africa & Middle East ,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.04 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 13 | g/10min | ISO 1133 |
| Shrinkage rate | Internal Method | ||
| — | 0.65 | % | Internal Method |
| 90℃，2 hrs | 0.10 | % | Internal Method |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30℃ | 4.2 | kJ/m² | ISO 179/1eA |
| -20℃ | 5.0 | kJ/m² | ISO 179/1eA |
| 23℃ | 40 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | ISO 179/1eU | ||
| -20℃ | 无断裂 | ISO 179/1eU | |
| 23℃ | 无断裂 | ISO 179/1eU | |
| Impact strength of cantilever beam notch | ISO 180/1A | ||
| -20℃ | 6.1 | kJ/m² | ISO 180-1A |
| 23℃ | 41 | kJ/m² | ISO 180-1A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 92.0 | ℃ | ISO 75-2/B |
| 1.8 MPa, unannealed | 50.0 | ℃ | ISO 75-2/A |
| Vicat Softening Temp | |||
| A50 | 121 | ℃ | ISO 306/A50 |
| B50 | 38.0 | ℃ | ISO 306 |
| Linear coefficient of thermal expansion | |||
| MD：-30~80℃ | 5.0E-5 | 1/℃ | Internal Method |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Ball hardness | |||
| H 132/10 | 26.0 | MPa | ISO 2039-1 |
| Tensile modulus | 1400 | MPa | ISO 527-1-2 |
| tensile strength | |||
| yield | 16.0 | MPa | ISO 527-2/50 |
| Tensile strain | ISO 527-2/50 | ||
| yield | 7.0 | % | ISO 527-2/50 |
| fracture | > 300 | % | ISO 527-2/50 |
| Bending modulus | 1500 | MPa | ISO 178 |
| bending strength | 21.0 | MPa | ISO 178 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 | °C | |
| Drying time | 2.0 | hr | |
| Hopper temperature | 40 to 80 | °C | |
| Processing (melt) temperature | 220 to 260 | °C | |
| Mold temperature | 30 to 50 | °C | |
| Hold pressure | 30.0 to 60.0 | MPa | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |