| About |
|---|
| Examples of application SMT bobbins Coil bobbins Commutators Governors Various types of switch Relay bases Connectors Communications equipment parts&& |
| Product Description | |
|---|---|
| Generic | DAP增塑剂 |
| Material Status | Commercial: Active |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.90 to 1.95 | g/cm³ | JIS K6911 |
| Shrinkage rate | 0.60 to 0.90 | % | JIS K6911 |
| Water absorption rate | |||
| boiling | 0.15 to 0.20 | % | JIS K6911 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| bending strength | |||
| injection molding | 147 to 167 | MPa | JIS K6911 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| injection molding | 5.9 to 7.8 | kJ/m² | JIS K6911 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | 240 to 250 | ℃ | JIS K6911 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Dielectric strength | 12 to 14 | kV/mm | JIS K6911 |
| Dielectric constant | 4.30 to 4.60 | JIS K6911 | |
| Dissipation factor | 0.010 to 0.015 | JIS K6911 | |
| Arc resistance | > 140 | sec | JIS K6911 |
| Compared to the leakage tracing index | > 600 | V | IEC 60112 |
| insulation resistance | |||
| After boiling | 1.0E+13 to 1.0E+14 | ohms | |
| at ordinary state | 1.0E+14 to 1.0E+15 | ohms |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 0.38 mm | V-0 | UL 94 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Injection Molding |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |