About |
---|
Deltron 5365 is a Polyphenylene Sulfide (PPS) material. It is available in Asia Pacific for injection molding. Important attributes of Deltron 5365 are: Flame Rated Wear Resistant&& |
Product Description | |
---|---|
Supplier | Lin Gen |
Generic | PPS |
Material Status | Commercial: Active |
Features | Good wear resistance,V-0 |
Availabilitys | Asia Pacific |
Process Methods | Injection Molding |
Technical Data | |||
---|---|---|---|
PHYSICAL | Nominal value | Unit | Test method |
Density | 1.80 | g/cm³ | |
Shrinkage rate | |||
MD | 0.20 to 0.50 | % | |
Water absorption rate | |||
balance | 0.020 | % |
IMPACT | Nominal value | Unit | Test method |
---|---|---|---|
Impact strength of cantilever beam notch | 9.00 | kJ/m² |
THERMAL | Nominal value | Unit | Test method |
---|---|---|---|
Hot deformation temperature | |||
1.8 MPa, unannealed | 265 | ℃ | |
Melting temperature | 285 | ℃ | |
Linear coefficient of thermal expansion | |||
MD | 1.9E-5 | 1/℃ |
Electrical performance | Nominal value | Unit | Test method |
---|---|---|---|
Surface resistivity | 1.2E+14 | ohms | |
Volume resistivity | 2.5E+16 | ohms·cm | |
Dielectric strength | 15 | kV/mm | |
Dielectric constant | |||
1 MHz | 3.20 |
FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
---|---|---|---|
Flame retardant level | |||
2.00 mm | V-0 |
MECHANICAL | Nominal value | Unit | Test method |
---|---|---|---|
Rockwell hardness | |||
R-level | 100 | ||
tensile strength | 130 | MPa | |
Tensile strain | |||
fracture | 1.6 | % | |
Bending modulus | 12000 | MPa | |
bending strength | 190 | MPa | |
compressive strength | 150 | MPa |
Process Conditions | |||
---|---|---|---|
injection | Nominal value | Unit | Test method |
Drying temperature | 120 to 140 | °C | |
Drying time | 4.0 to 8.0 | hr | |
Barrel rear temperature | 240 to 260 | °C | |
Barrel middle temperature | 290 to 310 | °C | |
Barrel front temperature | 300 to 330 | °C | |
Mold temperature | 100 to 140 | °C |
Notes |
---|
1. Typical properties: these are not to be construed as specifications. |
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |