| About |
|---|
| PP, 40% glass fiber reinforced, not Flame Retardant compound, very good mechanical properties, chemically bonded, thermostabilized, GWFI 650/1-2 GWIT 775/1-2.&& |
| Product Description | |
|---|---|
| Generic | PP not specified |
| Material Status | Commercial: Active |
| Features | Heat Stabilized,HB |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.21 | g/cm³ | ASTM D792 |
| Shrinkage rate | ASTM D955 | ||
| MD | 0.30 | % | ASTM D955 |
| TD | 0.70 | % | ASTM D955 |
| Water absorption rate | |||
| saturated | 0.020 | % | ASTM D570 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 8000 | MPa | ASTM D638 |
| tensile strength | |||
| yield | 90.0 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 2.0 | % | ASTM D638 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | 9.0 | kJ/m² | ISO 180/A |
| Notched impact strength of cantilever beam | 35 | kJ/m² | ISO 180 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 150 | ℃ | ASTM D648-A |
| Vicat Softening Temp | 145 | ℃ | ASTM D1525 2 |
| Relative temperature index | 120 | ℃ | UL 746 |
| Electrical performance | 120 | ℃ | UL 746 |
| Impact mechanical performance | 120 | ℃ | UL 746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Compared to the leakage tracing index | 600 | V | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 1.60 mm | HB | UL 94 | |
| 3.20 mm | HB | UL 94 | |
| Glowing wire flammability index | |||
| 1.0-2.0 mm | 650 | ℃ | IEC 60695-2-12 |
| Igniting temperature of the hot wire | |||
| 1-2 mm | 675 | ℃ | IEC 60695-2-13 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 70 | °C | |
| Drying time | 3.0 | hr | |
| Processing (melt) temperature | 220 | °C | |
| Mold temperature | 70 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Loading 2 (50 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |