Derakane® 470-36-S

About
DERAKANE 470-36-S epoxy vinyl ester resin is an epoxy novolac-based resin designed to provide exceptional thermal and chemical resistance properties at higher temperatures. This resin offers a high resistance to solvents and chemicals, good retention of strength and toughness at elevated temperatures, and excellent resistance to acidic oxidizing environments. APPLICATIONS AND USE Equipment fabricated with DERAKANE 470-36-S resin is suitable for such applications as high temperature flue gas desulfurization processes, industrial waste treatment facilities, metal pickling and solvent extraction processes used in mining. DERAKANE 470-36-S resin is recommended for most FRP fabrication processes including hand lay-up, spray-up, pultrusion, infusion and resin transfer molding. Its stability makes it suitable for the formulation of special coatings like flake glass coatings.&&

About

DERAKANE 470-36-S epoxy vinyl ester resin is an epoxy novolac-based resin designed to provide exceptional thermal and chemical resistance properties at higher temperatures. This resin offers a high resistance to solvents and chemicals, good retention of strength and toughness at elevated temperatures, and excellent resistance to acidic oxidizing environments. APPLICATIONS AND USE Equipment fabricated with DERAKANE 470-36-S resin is suitable for such applications as high temperature flue gas desulfurization processes, industrial waste treatment facilities, metal pickling and solvent extraction processes used in mining. DERAKANE 470-36-S resin is recommended for most FRP fabrication processes including hand lay-up, spray-up, pultrusion, infusion and resin transfer molding. Its stability makes it suitable for the formulation of special coatings like flake glass coatings.&&

Product Description
Generic	乙烯基酯
Material Status	Commercial: Active
Features	Acidproof,High Heat Resistance,Solvent resistance
Availabilitys	Europe

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.15	g/cm³	ASTM D792 , ISO 1183
Solution viscosity	240	mPa·s
styrene content	36	%

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
1.8 MPa, unannealed	146	℃	ASTM D648
1.8 MPa, unannealed	145	℃	ISO 75-2/A

Supplementary information	Nominal value	Unit	Test method
Volume contraction	8.9	%

MECHANICAL	Nominal value	Unit	Test method
Babbitt hardness	40		ASTM D2583
Tensile modulus
—	3590	MPa	ASTM D638
—	3600	MPa	ISO 527-2
tensile strength
—	89.6	MPa	ASTM D638
—	90.0	MPa	ISO 527-2
Tensile strain
yield	3.0 to 4.0	%	ASTM D638 , ISO 527-2
Bending modulus
—	3790	MPa	ASTM D790
—	3800	MPa	ISO 178
bending strength
—	159	MPa	ASTM D790
—	160	MPa	ISO 178

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.