Derakane® 510A-40

About
DERAKANE 510A-40 epoxy vinyl ester resin is a brominated bisphenol-A based vinyl ester, designed to offer the maximum degree of fire retardance”) combined with enhanced chemical resistance and toughness. Since fire retardance is achieved without additives, chemical resistance is maintained and visual inspection of fabricated articles is not impaired. It offers the highest bromine content of any DERAKANE resin. APPLICATIONS AND USE DERAKANE 510A-40 resin is the preferred choice where the highest fire retardance is required and is the standard recommendation for external fire retardance layer on FRP equipment. DERAKANE 510A-40 resin is used extensively in FRP ductwork, stacks and stack liner applications, handling mixtures of air and hot gases of potentially flammable liquids. It can be used with filament winding, hand lay-up, spray-up, pultrusion, and resin transfer molding techniques.&&

About

DERAKANE 510A-40 epoxy vinyl ester resin is a brominated bisphenol-A based vinyl ester, designed to offer the maximum degree of fire retardance”) combined with enhanced chemical resistance and toughness. Since fire retardance is achieved without additives, chemical resistance is maintained and visual inspection of fabricated articles is not impaired. It offers the highest bromine content of any DERAKANE resin. APPLICATIONS AND USE DERAKANE 510A-40 resin is the preferred choice where the highest fire retardance is required and is the standard recommendation for external fire retardance layer on FRP equipment. DERAKANE 510A-40 resin is used extensively in FRP ductwork, stacks and stack liner applications, handling mixtures of air and hot gases of potentially flammable liquids. It can be used with filament winding, hand lay-up, spray-up, pultrusion, and resin transfer molding techniques.&&

Product Description
Generic	乙烯基酯
Material Status	Commercial: Active
Features	Good flexibility,Alkali resistant,Corrosion Resistant,Flame Characteristics,Solvent resistance,Bromination
Availabilitys	North America,Europe

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Solution viscosity	400	mPa·s
styrene content	38	%

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
1.8 MPa, unannealed	104	℃	ASTM D648，ISO 75-2/A

MECHANICAL	Nominal value	Unit	Test method
Babbitt hardness	40		ASTM D2583
Tensile modulus
—	3380	MPa	ASTM D638
—	3400	MPa	ISO 527-2
tensile strength
—	84.8	MPa	ASTM D638
—	86.0	MPa	ISO 527-2
Tensile strain
yield	4.0 to 5.0	%	ASTM D638 , ISO 527-2
Bending modulus
—	3590	MPa	ASTM D790
—	3600	MPa	ISO 178
bending strength	150	MPa	ASTM D790，ISO 178

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.