Derakane® Momentum 510C-350

About
DERAKANE MOMENTUM® 510 C-350 is a brominated epoxy vinyl ester resin that offers a high degree of fire retardance while providing excellent chemical resistance and toughness. Optimum fire retardance is achieved when antimony compounds are added to the resin. Laminates made with DERAKANE MOMENTUM 510 C-350 resin have met ASTM E-84 Flame Spread “Class 2” rating (less than 75). With the use of antimony synergists, “Class 1” ratings can be achieved. APPLICATIONS AND USE DERAKANE MOMENTUM 510 C-350 resin is designed for ease of fabrication using hand lay-up, spray-up, filament winding, compression molding, resin transfer molding and pultrusion techniques. This resin is used extensively in FRP duct work, stacks and stack-liner applications. It is also suitable for equipment handling mixtures of air and hot gases, building panels and flooring compounds where a degree of ignition inhibiting properties are needed. DERAKANE MOMENTUM 510 C-350 resin resists mechanical and chemical damage enabling use in various caustic environments such as sodium hypochlorite, chlorine dioxide and alkaline hydrogen peroxide.&&

About

DERAKANE MOMENTUM® 510 C-350 is a brominated epoxy vinyl ester resin that offers a high degree of fire retardance while providing excellent chemical resistance and toughness. Optimum fire retardance is achieved when antimony compounds are added to the resin. Laminates made with DERAKANE MOMENTUM 510 C-350 resin have met ASTM E-84 Flame Spread “Class 2” rating (less than 75). With the use of antimony synergists, “Class 1” ratings can be achieved. APPLICATIONS AND USE DERAKANE MOMENTUM 510 C-350 resin is designed for ease of fabrication using hand lay-up, spray-up, filament winding, compression molding, resin transfer molding and pultrusion techniques. This resin is used extensively in FRP duct work, stacks and stack-liner applications. It is also suitable for equipment handling mixtures of air and hot gases, building panels and flooring compounds where a degree of ignition inhibiting properties are needed. DERAKANE MOMENTUM 510 C-350 resin resists mechanical and chemical damage enabling use in various caustic environments such as sodium hypochlorite, chlorine dioxide and alkaline hydrogen peroxide.&&

Product Description
Generic	乙烯基酯
Material Status	Commercial: Active
Features	Good flexibility,Alkali resistant,Corrosion Resistant,Flame Characteristics,Acidproof,Solvent resistance,Bromination
Availabilitys	Africa & Middle East ,North America,Latin America,Asia Pacific,Europe

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Solution viscosity	420	mPa·s
styrene content	35	%

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
1.8 MPa, unannealed	104	℃	ASTM D648
1.8 MPa, unannealed	105	℃	ISO 75-2/A
Glass transition temperature
—	121	℃	ASTM D3418
—	120	℃	ISO 11357-2

Supplementary information	Nominal value	Unit	Test method
Volume contraction	7.8	%

MECHANICAL	Nominal value	Unit	Test method
Babbitt hardness	35		ASTM D2583
Tensile modulus
—	3170	MPa	ASTM D638
—	3200	MPa	ISO 527-2
tensile strength
—	82.7	MPa	ASTM D638
—	86.0	MPa	ISO 527-2
Tensile strain
yield	5.0 to 6.0	%	ASTM D638 , ISO 527-2
Bending modulus
—	3380	MPa	ASTM D790
—	3400	MPa	ISO 178
bending strength
—	152	MPa	ASTM D790
—	150	MPa	ISO 178

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.