DESLON™ 6 DSC102G6

About
Descriptions: DESLON™ DSC102G6 is one of the brands which made by Polyamide6 that filled Glass Fiber 30% and reinforces goods. It provides good mechanical property, excellent injection molding property and fluidity property. Applications:DESLON™ DSC102G6 is one of the most-used for high impact resistance and heat-resisting property goods, such as Electronic & Automotive Bracket, Outside Handle Base etc.&&

About

Descriptions: DESLON™ DSC102G6 is one of the brands which made by Polyamide6 that filled Glass Fiber 30% and reinforces goods. It provides good mechanical property, excellent injection molding property and fluidity property. Applications:DESLON™ DSC102G6 is one of the most-used for high impact resistance and heat-resisting property goods, such as Electronic & Automotive Bracket, Outside Handle Base etc.&&

Product Description
Supplier	DESCO
Generic	PA6
Material Status	Commercial: Active
Features	High impact resistance,Good liquidity,High Heat Resistance,HB
Availabilitys	Asia Pacific
Process Methods	Injection Molding

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.35	g/cm³	ASTM D792
Shrinkage rate
MD	0.40 to 0.70	%
Water absorption rate
23℃，24hr	1.3	%	ASTM D570

IMPACT	Nominal value	Unit	Test method
Impact strength of cantilever beam notch	120	J/m	ASTM D256

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature			ASTM D648
0.45 MPa, unannealed	220	℃	ASTM D648
1.8 MPa, unannealed	210	℃	ASTM D648
Melting temperature	220	℃	DSC

Electrical performance	Nominal value	Unit	Test method
Volume resistivity	2.0E+12	ohms·cm	ASTM D257
Dielectric strength	20	kV/mm	ASTM D149
Dielectric constant
1 MHz	4.00		ASTM D150
Arc resistance	160	sec	ASTM D495

FLAME CHARACTERISTICS	Nominal value	Unit	Test method
Flame retardant level	HB		UL 94

MECHANICAL	Nominal value	Unit	Test method
Rockwell hardness
R-level	121		ASTM D785
tensile strength	167	MPa	ASTM D638
Tensile strain
fracture	3.0	%	ASTM D638
Bending modulus	7850	MPa	ASTM D790
bending strength	235	MPa	ASTM D790

Process Conditions
injection	Nominal value	Unit	Test method
Drying temperature	80 to 120	°C
Drying time	3.0 to 5.0	hr
Recommended maximum moisture content	< 0.20	%
Barrel rear temperature	240 to 250	°C
Barrel middle temperature	250 to 260	°C
Barrel front temperature	250 to 270	°C
Nozzle temperature	255 to 270	°C
Processing (melt) temperature	255 to 270	°C
Mold temperature	80 to 100	°C

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.