| About |
|---|
| Descriptions: DESLON™ DSC210IR is one of the brands which made by Polyamide66 and unreinforced goods. It provides high mechanical strength, high impact resistance and excellent injection molding property. Applications: DESLON™ DSC210IR is one of the most-used resin requested for mechanical strength, impact resistance and goods injection molding property, such as Fuse Box, Height Knob of Automotive parts.&& |
| Product Description | |
|---|---|
| Supplier | DESCO |
| Generic | PA66 |
| Material Status | Commercial: Active |
| Features | Good Rigidity,High impact resistance,HB |
| Availabilitys | Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.11 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| MD | 1.7 to 2.3 | % | |
| Water absorption rate | |||
| 23℃，24hr | 1.3 | % | ASTM D570 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | 150 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 0.45 MPa, unannealed | 220 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed | 65.0 | ℃ | ASTM D648 |
| Melting temperature | 260 | ℃ | DSC |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1.0E+14 | ohms·cm | ASTM D257 |
| Dielectric strength | 24 | kV/mm | ASTM D149 |
| Dielectric constant | |||
| 1 MHz | 3.10 | ASTM D150 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | HB | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 115 | ASTM D785 | |
| tensile strength | 61.8 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 50 | % | ASTM D638 |
| Bending modulus | 2160 | MPa | ASTM D790 |
| bending strength | 84.3 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 to 100 | °C | |
| Drying time | 4.0 to 5.0 | hr | |
| Recommended maximum moisture content | < 0.20 | % | |
| Barrel rear temperature | 270 to 280 | °C | |
| Barrel middle temperature | 280 to 285 | °C | |
| Barrel front temperature | 285 to 290 | °C | |
| Nozzle temperature | 280 to 285 | °C | |
| Processing (melt) temperature | 280 to 285 | °C | |
| Mold temperature | 80 to 120 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |