| Descriptions: DESLON™ DSC214GM is one of the brands which made by Polyamide66 that filled Glass Fiber/Mineral Filler 35% and reinforced goods. It provides high mechanical strength property, modification resistance, good surface appearance, thermal property. Applications: DESLON TM DSC214GM is one of the most-used resin requested for high mechanical strength, good surface appearance, thermal property goods, such as Cylinder Head cover of automotive parts.&& |
| Product Description | |
|---|---|
| Supplier | DESCO |
| Generic | PA66 |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good Dimensional Stability,Heat Stabilized,HB |
| Availabilitys | Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.43 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| MD | 0.60 to 1.0 | % | |
| Water absorption rate | |||
| 23℃，24hr | 0.70 | % | ASTM D570 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | 49 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 0.45 MPa, unannealed | 255 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed | 235 | ℃ | ASTM D648 |
| Melting temperature | 260 | ℃ | DSC |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1.0E+14 | ohms·cm | ASTM D257 |
| Dielectric strength | 23 | kV/mm | ASTM D149 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | HB | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 124 | ASTM D785 | |
| tensile strength | 108 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 4.0 | % | ASTM D638 |
| Bending modulus | 6370 | MPa | ASTM D790 |
| bending strength | 172 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 to 100 | °C | |
| Drying time | 4.0 to 5.0 | hr | |
| Recommended maximum moisture content | < 0.20 | % | |
| Barrel rear temperature | 275 to 285 | °C | |
| Barrel middle temperature | 285 to 290 | °C | |
| Barrel front temperature | 285 to 295 | °C | |
| Nozzle temperature | 285 to 295 | °C | |
| Processing (melt) temperature | 285 to 295 | °C | |
| Mold temperature | 80 to 120 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |