Descriptions: DESLON™ DSC223G6 is one of the brands which made by Polyamide66 that filled Glass Fiber 33% and reinforced goods. It provides high mechanical strength, good fluidity property and good injection molding property. Applications: DESLON™ DSC223G6 is one of the most-used resin requested for high mechanical strength, thermal property goods, such as Actuator Motor Case of Automotive parts.&&

About

Descriptions: DESLON™ DSC223G6 is one of the brands which made by Polyamide66 that filled Glass Fiber 33% and reinforced goods. It provides high mechanical strength, good fluidity property and good injection molding property. Applications: DESLON™ DSC223G6 is one of the most-used resin requested for high mechanical strength, thermal property goods, such as Actuator Motor Case of Automotive parts.&&

Product Description
Supplier	DESCO
Generic	PA66
Material Status	Commercial: Active
Features	Good Rigidity,Good liquidity,Heat Stabilized,HB
Availabilitys	Asia Pacific
Process Methods	Injection Molding

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.40	g/cm³	ASTM D792
Shrinkage rate
MD	0.40 to 0.80	%
Water absorption rate
23℃，24hr	0.60	%	ASTM D570

IMPACT	Nominal value	Unit	Test method
Impact strength of cantilever beam notch	120	J/m	ASTM D256

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature			ASTM D648
0.45 MPa, unannealed	255	℃	ASTM D648
1.8 MPa, unannealed	250	℃	ASTM D648
Melting temperature	260	℃	DSC

Electrical performance	Nominal value	Unit	Test method
Volume resistivity	1.0E+14	ohms·cm	ASTM D257
Dielectric strength	25	kV/mm	ASTM D149
Dielectric constant
1 MHz	4.00		ASTM D150
Arc resistance	120	sec	ASTM D495

FLAME CHARACTERISTICS	Nominal value	Unit	Test method
Flame retardant level	HB		UL 94

MECHANICAL	Nominal value	Unit	Test method
Rockwell hardness
R-level	123		ASTM D785
tensile strength	196	MPa	ASTM D638
Tensile strain
fracture	3.0	%	ASTM D638
Bending modulus	9810	MPa	ASTM D790
bending strength	265	MPa	ASTM D790

Process Conditions
injection	Nominal value	Unit	Test method
Drying temperature	80 to 100	°C
Drying time	4.0 to 5.0	hr
Recommended maximum moisture content	< 0.20	%
Barrel rear temperature	270 to 280	°C
Barrel middle temperature	280 to 285	°C
Barrel front temperature	285 to 290	°C
Nozzle temperature	280 to 285	°C
Processing (melt) temperature	280 to 285	°C
Mold temperature	80 to 120	°C

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.