| About |
|---|
| Descriptions: DESLOY™ DSC940B is PC & PBT alloy resin which has an advantage of both resins. It has good mechanical property and impact resistance in low temperature. Applications: DESLOY™ DSC940B is suitable for automotive parts which request good mechanical property and low deformation property.&& |
| Product Description | |
|---|---|
| Supplier | DESCO |
| Generic | PC+PBT |
| Material Status | Commercial: Active |
| Features | Good Dimensional Stability,low-temperature impact resistance,HB |
| Availabilitys | Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.22 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| MD | 0.70 to 1.0 | % | |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | 690 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 0.45 MPa, unannealed | 110 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed | 95.0 | ℃ | ASTM D648 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | HB | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 110 | ASTM D785 | |
| tensile strength | 58.8 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 100 | % | ASTM D638 |
| Bending modulus | 2260 | MPa | ASTM D790 |
| bending strength | 83.4 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 100 to 120 | °C | |
| Drying time | 3.0 to 5.0 | hr | |
| Recommended maximum moisture content | < 0.20 | % | |
| Barrel rear temperature | 260 to 270 | °C | |
| Barrel middle temperature | 270 to 280 | °C | |
| Barrel front temperature | 270 to 280 | °C | |
| Nozzle temperature | 270 to 280 | °C | |
| Processing (melt) temperature | 270 to 280 | °C | |
| Mold temperature | 60 to 90 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |