| About |
|---|
| injection molding grade; grease and oil-resistant; low compression set; good heat resistance; high elasticity; short cycle times; Application; Automotive engineering; Technical parts; Bearing bushes&& |
| Product Description | |
|---|---|
| Supplier | Covestro |
| Generic | TPU-酯 |
| Material Status | Commercial: Active |
| Features | Good Dimensional Stability,High elastic,Quick molding cycle,High Heat Resistance,Grease resistance |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.22 | g/cm³ | ISO 1183-3 |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tear strength | 150 | kN/m | ISO 34-1 |
| Compression deformation | ISO 815 | ||
| 23℃，72 hr | 25 | % | ISO 815 |
| 70℃，24 hr | 35 | % | ISO 815 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact Resilience | 35 | % | ISO 4662 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | ISO 868 3 | ||
| Shore A, 3 seconds | 97 | ISO 868 3 | |
| Shore D, 15 seconds | 59 | ISO 868 3 | |
| tensile strength | DIN 53504 | ||
| Fracture, 23 ℃ | 42.5 | MPa | DIN 53504 |
| 10% strain, 23 ℃ | 15.1 | MPa | DIN 53504 |
| 50% strain, 23 ℃ | 22.5 | MPa | DIN 53504 |
| 300% 应变, 23°C | 35.1 | MPa | DIN 53504 |
| Tensile strain | |||
| Fracture, 23 ℃ | 390 | % | DIN 53504 |
| Bending modulus | 170 | MPa | ISO 178 |
| Tensile storage modulus | ISO 6721-1,-4 | ||
| -20℃ | 1.76 | GPa | ISO 6721-1,-4 |
| 20℃ | 0.446 | GPa | ISO 6721-1,-4 |
| 60℃ | 0.130 | GPa | ISO 6721-1,-4 |
| abrasion resistance | |||
| 23℃ | 40.0 | mm³ | ISO 4649-A |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | < 110 | °C | |
| Processing (melt) temperature | 235 to 245 | °C | |
| Mold temperature | 20 to 40 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 3. 7.9 in/min |
| 4. 0.079 in/min |
| 5. Method A |
| 6. 20 in/min |
| 7. Method C |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |